In this work, homogeneous thermochemical co-precipitation method was used to fabricate W-25wt%Cu nanocomposite. Synthesized nanocomposite powder was calcined and reduced. A hydrogen atmosphere sintering at 1200oC for 105 consolidated the product up to a density close to 98% theoretical density. Wear experiment were carried out using a pin-ondisc set up at three normal loads of 5, 10 and 15 N an...

In this work, homogeneous thermochemical co-precipitation method was used to fabricate W-25wt%Cu nanocomposite. Synthesized nanocomposite powder was calcined and reduced. A hydrogen atmosphere sintering at 1200oC for 105 consolidated the product up to a density close to 98% theoretical density. Wear experiment were carried out using a pin-ondisc set up at three normal loads of 5, 10 and 15 N an...

Rights: © 2014 Elsevier. This is the post print version of the following article: Saikko, Vesa. 2014. Effect of shelf versus accelerated aging of UHMWPE on delamination in knee wear simulation. Tribology International. Volume 73, May 2014. 10-16. ISSN 0301-679X (printed). DOI: 10.1016/j.triboint.2014.01.001, which has been published in final form at http://www.sciencedirect.com/science/article/...

Wear of total knee replacement continues to be a significant factor influencing the clinical longevity of implants. Historically, failure due to delamination and fatigue directed design towards more conforming inserts to reduce contact stress. As new generations of more oxidatively stable polyethylene have been developed, more flexibility in bearing design has been introduced. The aim of this s...

INTRODUCTION Wear and fracture of patellar components has been reported in the literature as a failure mode for both cemented and press fit patellar components [1-5]. Malalignment of the patellar components can cause higher contact stresses, which can lead to excessive wear, delamination, and/or fracture of the component. Therefore, in vitro testing of the patella in a clinically relevant malal...

accumulative roll bonding (arb) was used to fabricate the cu-zn multilayer and cu-zn solid solution. a lamellar structure with the hardness of about 130 vhn was formed after eight arb cycles. following to the suitable heat treatment, a solid solution with a uniform microstructure and hardness of about 57 vhn was produced. the dominant wear mechanism in the arb processed multilayer was found to ...

Si-incorporated diamond-like carbon (Si-DLC) coatings ranging from 0 to 2 at % Si were deposited on Ti-alloy substrate by means of radio frequency plasma-assisted chemical vapor deposition (r.f. PACVD) technique, using a mixture of benzene (C(6)H(6)) and silane (SiH(4)) as the reaction gas. The synergy in wear and corrosion of Si-DLC coatings was investigated by tribological and electrochemical...

Carbon fiber reinforced plastics (CFRP) have good physical properties, such as high specific strength and high specific modulus. However, cutting delamination, tearing and burr, etc. often occur in the machining process of CFRP, which results in the uncontrollability of machining surface quality and serious tool wear. In this paper, milling of CFRP with a staggered cutter was carried out, the c...

Diamond coated cutting tools have been pursued as a costeffective substitute to brazed polycrystalline diamond (PCD) tools in applications such as machining high-strength and lightweight materials. However, coating delamination has been known as the major failure mode of diamond coated tools, which terminates tool life prematurely. Once delamination failure occurs, the tool substrate often subj...

We report exceptional nanoscale wear and fouling resistance of ultrananocrystalline diamond (UNCD) tips integrated with doped silicon atomic force microscope (AFM) cantilevers. The resistively heated probe can reach temperatures above 600 degrees C. The batch fabrication process produces UNCD tips with radii as small as 15 nm, with average radius 50 nm across the entire wafer. Wear tests were p...