This study was designed to evaluate the efficacy of resin coating on the regional microtensile bond strength (MTBS) of a resin cement to the dentin walls of Class II cavities. Twenty mesio-occlusal cavities were prepared in human molars. In 10 cavities, a resin coating consisting of a self-etching primer bonding system, Clearfil SE Bond, and a low-viscosity microfilled resin, Protect Liner F, w...

OBJECTIVES The aim of this study was to evaluate the influence of two adhesive systems and the post space region on the degree of conversion of dual resin cement and its bond strength to root dentin. MATERIAL AND METHODS One three-step etch-and-rinse (All-bond 2, Bisco) and another one-step self-etch (Xeno III, Dentsply) adhesive systems were applied on 20 (n=10) crownless bovine incisors, at...

This study evaluated the influence of curing method and storage condition on the microhardness of dual-cure resin cements: Panavia F 2.0 (PF) and Nexus 2 (NX). The specimens were either light-cured (LC) or chemically cured in darkness (CC). After 24 hours of storage in dry chamber (Dry) or distilled water (DW), the specimens were sectioned and polished. The microhardness of resin cement matrix ...

This investigation evaluated the effect of resin composite inlay/onlay thickness on the hardness of a group of eight dual-cure resin-based cements. Fourteen disc specimens measuring 6 mm in diameter and 2.5 mm thick were prepared from each of eight dual-cure cements: Adherence, Choice, Duolink, Enforce, Lute-It, Nexus, Resinomer and Variolink. Two specimens from each material were directly ligh...

The aim of this study was to evaluate the Knoop hardness after 15 min and 24 h of different shades of a dual-cured resin-based cement after indirect photoactivation (ceramic restoration) with 2 light-curing units (LCUs). The resin cement Variolink II (Ivoclar Vivadent) shade XL, A2, A3 and opaque were mixed with the catalyst paste and inserted into a black Teflon mold (5 mm diameter x 1 mm high...

OBJECTIVES To compare microhardness along the root canal post space of two resin cements in different shades and a dual-cure resin core material. STUDY DESIGN Root canals of 21 bovine incisors were prepared for post space. Translucent posts (X∘Post, Dentsply DeTrey) were luted using one the following resin luting agent: Calibra (Dentsply DeTrey) in Translucent, Medium and Opaque shades, RelyX...

OBJECTIVE Due to increasing of aesthetic demand, ceramic crowns are widely used in different situations. However, to obtain long-term prognosis of restorations, a good conversion of resin cement is necessary. To evaluate the degree of conversion (DC) of one light-cure and two dual-cure resin cements under a simulated clinical cementation of ceramic crowns. MATERIAL AND METHODS Prepared teeth ...

AIM To measure the light transmission through different esthetic posts and to evaluate the degree of polymerization of dual cure resin cement cured through these posts. MATERIALS AND METHODS The posts were divided into two experimental groups i.e. Group A (D.T. Light post); Group B (D.T. White post) and control i.e. Group C (metal post), each group having 10 samples. Posts of each group were ...

PURPOSE Adequate polymerization is a crucial factor in obtaining optimal physical properties and a satisfying clinical performance from composite resin materials. The aim of this study was to evaluate the polymerization efficiency of dual-cure resin cement cured with two different light curing units under zirconia structures having differing thicknesses. MATERIALS AND METHODS 4 zirconia discs...