zno and mn-zno nano powders were prepared by the sol-gel auto combustion method. the products were characterized by x-ray diffraction (xrd), energy dispersive analysis of x-ray (edx) and scanning electron microscopy (sem). structural and morphological properties of nano particles were investigated and the average crystalline size of zno and mn-doped zno was obtained 44 and 51 nm, respectively. ...

Calcium doped nickel ferrite powders have been prepared by sol-gel combustion technique. Metal nitrates, such as calcium nitrate, nickel nitrate and ferric nitrate, were used as the source materials and citric acid and polyvinyl alcohol were used as the burning agent and agglomeration reducing agent, respectively. The average crystallite size of the prepared ferrite was in the order of ~70- 92 ...

Calcium doped nickel ferrite powders have been prepared by sol-gel combustion technique. Metal nitrates, such as calcium nitrate, nickel nitrate and ferric nitrate, were used as the source materials and citric acid and polyvinyl alcohol were used as the burning agent and agglomeration reducing agent, respectively. The average crystallite size of the prepared ferrite was in the order of ~70- 92 ...

The role of iron in two modes of integration into alumina catalysts was studied at 0.39 wt% Fe and tested in trichloroethylene combustion. One modified alumina was synthesized using the sol-gel method with Fe added in situ during hydrolysis; another modification was performed using calcined alumina, prepared using the sol-gel method and impregnated with Fe. Several characterization techniques w...

the cunica nanopanicles have been synthesized by sol-gel auto-combusson. microwave and co-precipitationtechniques. then, the results of the three techniques were compared. in the vol-ael auto-combustion synthesiswas used glycine as a fuel. at first, sol was prepared. then, gel was achieved from drying so'. the prepared gelwas burnt at 350°c. in the noicrowavc technique, gel was prepared. then, ...

Highly sinterable alumina nano-powders have been synthesized by a sol-gel combustion method with glycine asfuel. The preparation involved the thermal decomposition of a chelating agent (fuel)-nitrate gel and theformation of amorphous precursors. The nanopowders calcined at 1100°C were characterized by X-ray powderdiffraction (XRD) and Scanning Electron Microscopy (SEM). It was found that the ch...