Corrosion of concrete reinforcing steel in highway structures has traditionally been related to chloride ions. However, another cause of reinforcing steel corrosion is concrete carbonation which decreases the pH of the pore solution, Carbonation-induced corrosion tends to develop later and proceeds at slower rates than chloride-induced corrosion. Since very long service life goals are currently...

To avoid the secondary pollution that inorganic corrosion inhibitor may cause in circulating cooling water, the bio-corrosion inhibition effect of lysozyme, catalase, lipase, and laccase, as the biologic inhibitors without the above problem, and the increased bio-corrosion inhibition effect of Ca+2 and Mg+2 are studied. An enzyme with corrosion properties was selected by rotary coupon test. The...

The wind turbine foundation serves as a permanent construction in the harsh marine corrosive environment, its anticorrosion design is essential to the safe use of the wind turbine structure. At present, there is a significant controversy over the local corrosion mechanism (such as pitting corrosion, and crevice corrosion) and its diffusion mechanism in the academic circle. In the paper, the Far...

Metallic coatings using thermal spraying techniques are widely applied to structural steels to protect infrastructure against corrosion and improve durability of the associated structures for longer service life. The thermal sprayed metallic coatings consisting of various metals, although have higher corrosion resistance, will still corrode in a long run and may also subject to corrosion induce...

This work tried to decide whether an occasionally observed falling of straw stalactites in the Moravian Karst caves is caused by a hypothetical chemical corrosion. The straw stalactite wall was found to be formed by three calcite layers. The middle layer (a stalactite skeleton) was typically cracked in agreement with calcite cleavage. Some impact of chemical corrosion was positively identified ...

Permeable reactive barriers containing zerovalent iron are being increasingly employed for in situ remediation of groundwater contaminated with redox active metals and chlorinated organic compounds. This research investigated the effect of chromate concentration on its removal from solution by zerovalent iron. Removal rates of aqueous Cr(VI) by iron wires were measured in batch experiments for ...

Environmental pollution caused by CO2 releasing from the production of cement is a great challenge for construction industry and has triggered exploration into more sustainable alternatives. Geopolymer Concrete (GPC) potential solution that does not involve use as binder. GPC produced mixing alumino-silicate source materials such fly-ash with alkali activators potassium hydroxide (KOH) silicate...

In some cases, a corrosion system may be exposed to radiation field. Most usually, it occurs as a part of atmospheric corrosion, when materials are, besides other factors, exposed also to visible and ultraviolet radiation. Technical significance of corrosion caused by such types of radiation is rather small. On the other hand, metallic materials may be exposed to high energy ionizing radiation ...

Stainless steel clad rebar (SCR) was investigated because it may become a cost-effective means of controlling corrosion in concrete under very aggressive environments. Sound SCR (316L cladding) resisted corrosion in saturated Ca(OH)2 solution (SCS) with up to 5 wt% chloride. Cladding breaks on SCR induced significant corrosion of exposed underlying CS in SCS with only 1 wt% chloride. A computer...

The filling of strand corrosion products during concrete crack propagation is investigated experimentally in the present paper. The effects of stirrups on the filling of corrosion products and concrete cracking are clarified. A prediction model of crack width is developed incorporating the filling proportion of corrosion products and the twisting shape of the strand. Experimental data on cracki...