The corrosion behaviour of αand β-Ta coatings was compared to that of Cr coatings produced by cylindrical magnetron sputtering as well as electrodeposition. For Ta coatings, the corrosion process was dominated by dissolution of the steel substrate through open pores, however, at the end of 5 days, coating degradation was not observed. In contrast, while open pores were not observed with the Cr ...