It is well known that in recent years magnetic materials have received increased attention due to their properties. For this reason a significant number of patents that were published during the last decade are oriented towards synthesis and study of such materials. The aim of this work is to create and study ferrite nanocrystalline materials with spinel structure, using sol-gel technology with...
The CuNiCA nanopanicles have been synthesized by sol-gel auto-combusson. microwave and co-precipitationtechniques. Then, the results of the three techniques were compared. In the vol-ael auto-combustion synthesiswas used glycine as a fuel. At first, sol was prepared. Then, gel was achieved from drying so'. The prepared gelwas burnt at 350°C. In the noicrowavc technique, gel was prepared. Then, ...
calcium doped nickel ferrite powders have been prepared by sol-gel combustion technique. metal nitrates, such as calcium nitrate, nickel nitrate and ferric nitrate, were used as the source materials and citric acid and polyvinyl alcohol were used as the burning agent and agglomeration reducing agent, respectively. the average crystallite size of the prepared ferrite was in the order of ~70- 92 ...
in this paper, labo3 perovskite type catalyst formulations were prepared by sol-gel auto combustion method using citric acid as the fuel. activity of catalysts was tested in catalytic oxidation of toluene as a model of volatile organic compounds. lacoo3 perovskite formulation showed the highest activity among labo3 (fe, mn and co) perovskite catalysts. so, lacoo3 perovskite based catalyst was s...
In this research the sol-gel auto-combustion method was used to prepare strontium hexaferrite nanopowder. A solution of distilled water, ferric and strontium nitrates, citric acid, trimethylamine, and n-decyltrimethylammonium bromide cationic surfactant, was heated to form a viscous gel. The gel was heated and then ignited automatically. As-burnt powder was calcined at temperatures from 700 to ...
zno and mn-zno nano powders were prepared by the sol-gel auto combustion method. the products were characterized by x-ray diffraction (xrd), energy dispersive analysis of x-ray (edx) and scanning electron microscopy (sem). structural and morphological properties of nano particles were investigated and the average crystalline size of zno and mn-doped zno was obtained 44 and 51 nm, respectively. ...
Cerium orthovanadate nanoparticles (CeVO4 NPs) were fabricated using urea-assisted facile sol-gel auto combustion method. X-ray diffraction (XRD) pattern revealed the crystal planes and size of synthesized CeVO4 NPs. The morphological shape and the crystalline nature of the NPs were examined by field emission scanning electron microscopy (FESEM). Energy-dispersive X-ray spectroscopy (EDX) affir...
zinc ferrite (znfe2o4) nanoparticles were synthesized via the auto-combustion assisted sol-gel method of zn2+ and fe3+ ions (molar ratio 1:2) in ammonia solution. the prepared nanomagnetic catalyst was characterized by ir, xrd, sem and icp. the diameter of the znfe2o4 mnps (63.7 nm) was determined by debye-scherre equation via their xrd pattern. nanomagnetic znfe2o4 efficiently catalyzes oxidat...
The dried nitrate-urea gels exhibit the combination of autoicatatric combustion behavior and ultrasonic, whichcan be used to synthesize the nanocatalyst ferrite powders. Cu and Ni Unites nanocatalyst powders sithcomposition of Caned], and NiFe204 were synthesized by a sol-gel auto catalnic combustion process. Themolar ratio between metal ions and urea was 11.2. The sob gel process was done at 8...