although cu and fe are immiscible under equilibrium conditions, they can form supersaturated solid solutions by mechanical alloying. in this paper, nano-structured of the metastable cu-fe phase containing 10, 15, 20 and 25% wt fe were synthesized by intensive ball milling for 15h, in order to achieve a solid solution of fe in cu. the phase composition, dissolution of the fe atoms into the cu ma...

Synthesis of dimethyl carbonate (DMC) from CO2 and methanol under milder reaction conditions was performed using reduced cerium oxide catalysts and reduced copper-promoted Ce oxide catalysts. Although the conversion of methanol was low (0.005-0.11%) for 2 h of reaction, DMC was synthesized as low as 353 K and at total pressure of as low as 1.3 MPa using reduced Cu-CeO2 catalyst (0.5 wt% of Cu)....

This study focused on the use of microbial potential for metal ion removal. Scenedesmus obliquus and Synechocystis sp. PCC 6803 were compared for accumulation of Cu in batch mode. During time course accumulation, S. obliquus accumulated Cu up to 124 μg mg -1 dry wt after 1h of incubation, whereas for Synechocystis sp. PCC 6803 it reached up to 64.9 μg mg -1 dry wt after 2h. Low biomass concentr...

Ag-28.1 wt. % Cu eutectic alloy solidifies in the form of eutectic dendrite at undercooling above 76 K. The remelting and ripening of the original lamellar eutectics result in the formation of the anomalous eutectics in the final microstructure. The addition of the third element Sb (0.5 and 1 wt. %) does not change the growth mode, but enlarges the volume fraction of anomalous eutectics because...

 Microsegregation is one of the most important phenomena occurs during solidification. It usually results in formation of some unexpected second phases which generally affect the mechanical properties and specially reduce the workability of casting products. The aim of this research is to study the effect of cooling rate and grain refinement on the microsegregation in Al-4.8 wt.% Cu. For this p...

An FeCoCrAlCu HEA coating was prepared on the surface of 45# steel by cold-spray-assisted induction remelting. The results showed that composed BCC and FCC phases. phase possessed an amplitude-modulated structure consisting a B1-disordered (FeCr) B2-ordered (AlCo), as well nanoscale precipitated near grain boundaries. solid solution Al–Cu matrix manifested characteristics typical twin structure...

Present work deals with the preparation of spark plasma-sintered Cu–Zn aggregate (5, 10 and 20 wt% Zn) with interfacial bonding only starting from elemental powders of Cu and Zn (99⋅9% purity) and subsequently making of porous template of Cu by dezincification. Sintering is done so as to achieve only interfacial bonding with the aim to maintain maximum potential difference between the Cu and Zn...