Alumina nanofibers were prepared by a technique that combined the sol-gel and electrospinning methods. The solution to be electrospun was prepared by mixing aluminum isopropoxide (AIP) in ethanol, which was then refluxed in the presence of an acid catalyst and polyvinylpyrolidone (PVP) in ethanol. The characterization results showed that alumina nanofibers with diameters in the range of 102 to ...

The control of particle size distribution of fabricated alumina nanoparticles from general alumina that has a large geometric standard deviation (GSD) is studied. A thermophoretic separator was used to control the GSD of the fabricated alumina nanoparticles. Unevaporated particles and primary particles were separated to yield a small GSD for fabricated alumina nanoparticles. The fabricated alum...

Alumina nanorods were prepared from chromium-containing alumina sludge, and the effects of doping elements, such as Cr, Fe, and Mg, were researched. The results show that the crystal transformation of alumina is restricted by the doped Cr and facilitated by the doped Fe and Mg, which is transformed from θ-Al2O3 to α-Al2O3 in the calcination process. Meanwhile, the crystal transformation of alum...

Aluminum saline slags is a waste of the metallurgical industry that presents serious environmental problems since it needs very extensive areas for its disposal, toxicity causes in atmosphere and groundwater, addition to high transportation costs. The valorization this residue by synthesis alumina, compound widely used chemical industry, generates impact great interest. In work, strategies synt...

Wettability alteration is one of the most important methods for oil recovery from sandstone and carbonate reservoirs. The effects of salinity, pH, temperature, and chemicals such as surfactants and fatty acids on the alteration of the wettability were described in previous studies. In recent years, attention has been directed to nanoparticles as a wettability alteration agent. The effect of som...

Cell adhesion, migration, and proliferation are significantly affected by the surface topography of the substrates on which the cells are cultured. Alumina is one of the most popular implant materials used in orthopedics, but few data are available concerning the cellular responses of mesenchymal stem cells (MSCs) grown on nanoporous structures. MSCs were cultured on smooth alumina substrates a...

Mesoporous alumina catalysts that incorporate nickel (Ni-Alumina) with different Ni/Al molar ratios of 1:2, 1:5 and 1:10 were synthesized by a one-step sol–gel method using lauric acid as a template. The prepared Ni-Alumina catalysts showed a relatively high surface area with a narrow pore size distribution after calcination at 700 ◦C; these effects were independent of the Ni/Al molar ratio. Al...

Nanoporous alumina membranes exhibit high pore densities, well-controlled and uniform pore sizes, as well as straight pores. Owing to these unusual properties, nanoporous alumina membranes are currently being considered for use in implantable sensor membranes and water purification membranes. Atomic layer deposition is a thin-film growth process that may be used to modify the pore size in a nan...

The paper reports a process for synthesis of γ-alumina from kaolin. Kaolin was transformed to meta-kaolin by calcination at 800 ̊C for 2h. γ-alumina powder was synthesized through extracting alumina from metakaolin via H2SO4 and meta-kaolin reactions and consequently precipitation in ethanol, which led to form the aluminum sulfate. The precipitated aluminum sulfate was dried and calcined at 900 ̊...

Many pioneers from around the world followed this initial experience but long-term results and good methodology were lacking. Recently, a number of reports 4-6 have focused attention again on an alumina-on-alumina combination. More than 30 years after its introduction into clinical practice, this article considers the current information on the alumina-on-alumina combination from both experimen...