Plasma electrolytic oxidation (PEO) was performed on a 1010 Aluminum alloy. To achieve thenanocomposite structure, Si3N4 nanoparticles were added into the electrolyte. In an alkaline aqueoussuspension (silicate-based), the effect of adding NiSO4 on the applied voltage, microstructure,composition, wear, and corrosion resistance of PEO coatings was investigated using ScanningElectron Microscopy (...

tarnish and corrosion behavior of three commercial dental amalgams namely am.1, am.2, am.3, have been investigated by utilizing in vitro tests. the corrosion and/or dissolution rate of the three dental amalgams were studied in 0.9 wt% nacl solution, artificial saliva and ringers solution. potentiodynamic polarization technique was employed to study cathodic and anodic polarization behavior, fro...

Corrosion inhibition of mild steel in 1 M HCl and 0.5 M H2SO4 by dapsone were studied by polarization resistance, Tafel polarization, electrochemical impedance spectroscopy (EIS) and weight loss measurement. Results obtained revealed that inhibition occurs through adsorption of the drug on metal surface without modifying the mechanism of corrosion process. Potentiodynamic polarization suggested...

Several experimental measurements are expressed in the form of one-dimensional profiles, for which there is a scarcity of methodologies able to classify the pertinence of a given result to a specific group. The polarization curves that evaluate the corrosion kinetics of electrodes in corrosive media are an application where the behavior is chiefly analyzed from profiles. Polarization curves are...

The electrochemical behavior of copper electrode in 2M potassium sulfide solution was studied using cyclic voltammograms and potentiostatic polarization techniques. The morphology studies were applied using scanning electron microscope (SEM) and energy dispersive analysis of X-rays (EDAX) and X-ray powder diffraction. Three anodic peaks were observed in the anodic scan of cyclic voltammograms. ...

In this paper, the electrochemical properties of MlNi Co Al electrode alloys, including high rate dischargeability, exchange 4.32x x 0.7 current density I , limiting current density I , and diffusion coefficient of hydrogen in the hydride D by means of linear polarization, 0 L a anodic polarization, and electrochemical impedance spectroscopy were systematically studied. The results indicate tha...

Passivation Phenomena have been observed upon cathodic and anodic polarization of the Al electrode in AlC 13-KCl-NaC1 melts between 100 and 160 °C. They are caused by formation of a solid salt layer at the electrode surface resulting from concentration changes upon current flow. The anodic limiting currents increased with temperature and with decreasing AlCl content of the melt. Current voltage...