The atmospheric corrosion of Mg and MgAl alloys was investigated. Corrosion tests were performed in the laboratory under controlled environment. CP Mg, AM50 and AZ91 samples were exposed at 95% RH and 22°C in the presence and in the absence of 400 ppm CO2 for 24 h to 672 h. The passive film was characterized by means of XPS, FTIR, AES and XRD. The film consisted of MgO/Mg(OH)2 with carbonate on...

Corrosion of reinforced concrete is one of the major problems in the construction industry causing premature deterioration of concrete structures well before their service life. This has placed incredible financial burden on many projects and also placed safety of users at risk. A research work was carried out to evaluate the effect of water cement ratio on corrosion of steel in reinforced conc...

The corrosion products of carbon steel and weathering steel exposed to three different types of atmospheres, at times ranging from one to three months, have been identified. The steels were exposed in an industrial site, an urban site (São Paulo City, Brazil), and a humid site. The effect of the steel type on the corrosion products formed in the early stages of atmospheric corrosion has been ev...

In this paper a functional graded material (FGM) thermal barrier coating (TBC) is prepared using Atmospheric Plasma Spraying (APS) method. The FGM layers were deposited by varying the feeding ratio of CYSZ/NiCrAlY and conventional CYSZ on a NiCrALY-coated Inconel 738 substrates. Hot corrosion behavior, bonding strength and the related failure mechanisms of a conventional TBC and a FGM TBC are i...

Weathering phenomena represent a topic of growing interest in computer graphics, and corrosion reactions are of great importance since they affect a large number of different fields. Previous investigations have essentially dealt with the modeling and rendering of metallic patinas. We propose an approach based on simple physical characteristics to simulate and render new forms of corrosion. We ...

The atmospheres in many cities along the coastal lines in the world have been rapidly changed to coastal-industrial atmosphere. Hence, it is vital to investigate the corrosion behavior of steel exposed to this kind of environment. In this present study, Electrochemical Impedance Spectrography (EIS) and film thickness measurement were applied to monitor the corrosion behavior of weathering steel...

Corrosion damage has been found in a number of nuclear power plant containment structures, and this could degrade the pressure capacity of the vessel. This has prompted concerns regarding the capacity of corroded containments to withstand accident loadings. For the low-carbon, low-strength steels used in containments, the effect of corrosion on material properties is discussed in this report, a...