Uniform 3 nm-sized ceria nanoparticles can protect against ischemic stroke by scavenging reactive oxygen species (ROS) and reducing apoptosis. PEGylated ceria nanoparticles showed protective effects against ROS-induced cell death in vitro. Optimal doses of ceria nanoparticles reduced infarct volumes and the rate of ischemic cell death in vivo.

Nanocrystalline ceria has been considered as support for carbon monoxide preferentially oxidation. In this study ceria was prepared by precipitation method and the effects of preparation conditions, such as pH of solution (8-10), aging time (1-12 hr), drying temperature (80-120 °C), calcination time (2-6 hr) and temperature (400-600 °C) were investigated on ceria synthesized powders properties....

The presence and release of nanoparticles (NPs) into the environment have important implications for human health and the environment. A critical aspect of the risk assessment of nanoparticles is to understand the interactions of manufactured nanoparticles with plants. In this study, the uptake and distribution characteristics of two types of ceria nanoparticles with sizes of ca. 7 nm and 25 nm...

We report here on the high activity and stability of low-content gold–cerium oxide catalysts for the water–gas shift reaction (WGS). These catalysts are reversible in cyclic reduction–oxidation treatment up to 400 8C, are non-pyrophoric, and are thus potential candidates for application to hydrogen generation for fuel cell power production. Low-content (0.2–0.9 at.%) gold–ceria samples were pre...

The catalytic activity of nanocrystalline doped ceria and Cuand Ag-modified ceria for the complete oxidation of methane was studied in this work. The catalyst structure was studied by X-ray diffraction (XRD) and related to the availability of low-temperature oxygen species. Selected samples were also analyzed by STEM/EDX, HRTEM, and XPS. Temperature-programmed reduction (TPR) by H2 and CH4, as ...

The effect of adding oxide promoters, at monolayer coverages, to Pd/ceria catalysts was studied for the watergas-shift reaction in 25 torr each of H2O and CO under differential conditions. Oxides of Fe, Tb, Gd, Y, Sn, Sm, Pr, Eu, Bi, Cr, V, Pb, and Mo were added to ceria by wet impregnation of aqueous salts and calcined to 873 K prior to addition of 1 wt% Pd. While most of the oxides had a negl...

Nanoceria is used as a catalyst in diesel fuel, as an abrasive in printed circuit manufacture, and is being pursued as an antioxidant therapeutic. Our objective is to extend previous findings showing that there were no reductions of cerium in organs of the mononuclear phagocyte (reticuloendothelial) system up to 30 days after a single nanoscale ceria administration. An ~5% aqueous dispersion of...

Low-content (<0.6 at.%) gold-ceria samples were prepared by one-pot synthesis by the urea gelation/co-precipitation method, and by sodium cyanide leaching of high-content (5 at.%) gold-ceria materials prepared by deposition–precipitation. These catalysts, containing cationic gold in ceria, are active for both the low-temperature water–gas shift (WGS) reaction and the preferential oxidation of C...

The role of Fe promoters has been investigated on Pd/ceria, Pt/ceria and Rh/ceria catalysts for the water-gas shift (WGS) reaction in 25 Torr of CO and H2O, under differential reaction conditions. While no enhancement was observed with Pt and Rh, the activity of Pd/ceria increased by as much as an order of magnitude upon the addition of an optimal amount of Fe. Similarly, the addition of 1 wt% ...

Novel interface-stabilized ceria nanophases have been grown on TiO2(110) by physical vapor deposition. At low coverage, dumbbell nanostructures constituted by reconstructed titania and ceria clusters are formed, while long range ordered nanoxides can be obtained by increasing the ceria dose. Scanning tunneling microscopy and photoemission spectroscopy were used to characterize the electronic pr...