In this paper, the stress intensity factor (SIF) variations along an arbitrarily developing crack front, the non-planar fatigue-crack growth patterns, and the fatigue life of a round bar with an initially straight-fronted surface crack, are studied by employing the 3D symmetric Galerkin boundary element method-finite element method (SGBEM-FEM) alternating method. Different loading cases, involv...

Environmentally dependent subcritical crack growth, or stress-corrosion cracking, along ceramic-metal interfaces is studied for the silica glass-copper system. Tests were conducted in various gaseous and liquid environments in order to determine their relative effects on stress-corrosion cracking and to gain some insight into the mechanisms that control interfacial crack growth. In agreement wi...

Pitting corrosion is one of the most common forms of localized corrosion. Corrosion pit results in a stress concentration and fatigue cracks usually initiate and propagate from these corrosion pits. Aging structures may fracture when the fatigue crack reaches a critical size. This paper experimentally simulates the effects of pitting morphologies on the static and fatigue behavior of steel bars...

Fatigue crack growth has been observed recently in ferroelectrics under cyclic electric loading[ Does the crack grow by electric breakdown\ or by the stress _eld near the crack tip< The present paper provides a mechanistic explanation for the electric!_eld!induced fatigue crack growth[ The non!uniform electric _eld near an insulated crack tip might cause domain switching which in turn produces ...

Mechanisms for fatigue crack closure under plane strain conditions have recently been identified at very low (near-threshold) stress intensities in terms of effects of excess corrosion deposits or fracture surface roughness in promoting premature closure of the crack. In the present paper, a geometric model is presented for crack closure induced by fracture surface roughness. This model specifi...

Abstract With the help of fractional differential equations, this article studies failure morphology, fatigue strength, and life corroded reinforced concrete beams under loading. Studies have shown that mid-span deflection low-corrosion is smaller than uncorroded beams. The corrosion-fatigue coupling effect accelerates crack growth rate steel bars. This reduces modulus causes stiffness beam to ...

This article presents a study of fatigue-crack propagation behavior in Nitinol, a 50Ni-50Ti (at. pct) superelastic/shape-memory alloy, with particular emphasis on the effect of the stress-induced martensitic transformation on crack-growth resistance. Specifically, fatigue-crack growth was characterized in stable austenite (at 120 8C), superelastic austenite (at 37 8C), and martensite (at 265 8C...

An evaluation of the fatigue crack resistance of human dentin was conducted to identify the degree of degradation that arises with aging and the dependency on tubule orientation. Fatigue crack growth was achieved in specimens of coronal dentin through application of Mode I cyclic loading and over clinically relevant lengths (0 ≤ a ≤ 2 mm). The study considered two directions of cyclic crack gro...