Final failure of laminated composite structures is preceded by different damage mechanisms involving fracture initiation and propagation. Fracture in a composite laminate can appear either between two plies or within a lamina. In the first case, interlaminar fracture or delamination, the crack causes separation of two adjacent plies and will mainly involve matrix failure or matrix-to-fibre debo...

In this paper, a two-dimensional computational model is proposed for predicting the initiation position and propagation path of subsurface crack of spur gear tooth flank. In order to simulate the contact of teeth, an equivalent model of two contacting cylinders is used. The problem is assumed to be under linear elastic fracture mechanic conditions and finite element method is used for numerical...

This paper presents a simple method based on strain energy density criterion to study the crack initiation angle by finite element method under biaxial loading condition. The crack surface relative displacement method is used to eliminate the calculation of the stress intensity factors which are normally required. The analysis is performed using higher order four node quadrilateral element. The...

Fatigue crack initiation and early short crack propagation behaviour in two microstructural variants of a recently developed Low Solvus, High Refractory (LSHR) disc superalloy at room temperature has been investigated by three-point bending with replication procedure. The results shows that fine gained (FG) LSHR possesses higher fatigue life due to its better crack initiation resistance, limite...

The present paper explores quasi-cleavage processes driven by dislocation pileups against a Dislocation Free Zone (DFZ). The nanoscopic growth of the main crack consists of sequences of nanocrack formation in DFZ and its subsequent linkage with the main crack. Under mode I loading, the equilibrium locations of individual dislocations and the equilibrium number of dislocations are determined by ...

Residual compressive stress can improve fretting fatigue strength. In this paper, the effects of residual stress on fretting fatigue of Al 2024-T351 alloy specimens are studied using a numerical approach. The extended finite element method combined with the cyclic cohesive zone model is adopted to model fretting fatigue crack growth behavior. It is shown that residual stress changes the frettin...

When a propagating cleavage front encounters a high-angle grain boundary it first penetrates through the grain boundary stably. With increasing penetration depth the resistance of the grain boundary rises, resulting in the well-known R-curve. When the balance between the rates of the energy release rate and the grain boundary resistance is reached, the crack advance becomes unstable and the gra...

In all-ceramic restorations, crack formation and propagation phenomena are of major concern, since they may result in intra-oral fracture. The objective of this study was calculation of damage in porcelain MOD inlays by utilization of a finite-element (FE) implementation of the distributed crack theory. "Damage" is defined as the parameter that describes the local decrease of stiffness caused b...

Knowledge of the mechanisms controlling crack formation, propagation and failure of FRCC under shear loading is currently limited. This paper presents a study that utilized photogrammetry to monitor the shear deformations of two FRCC materials and ordinary concrete (OC). Multiple shear cracks and strain hardening of both FRCC materials was observed under shear loading. The influence of fibers, ...

Existence of cracks in industrial structures is one of the important causes of their failure, especially when they are subjected to important axial compressive forces that might lead to buckling. Therefore, it must be considered in stress analysis and designing and loading of such structures. In this paper, the buckling and post-buckling behaviors of stainless-steel cracked plates under axial c...