Recently, a method for evaluating the fracture toughness of ceramics has been proposed by Fett based on the computed crack-opening displacements of cracks emanating from Vickers hardness indentations. To verify this method, experiments have been conducted to determine the toughness of a commercial silicon carbide ceramic, Hexoloy SA, by measuring the crack-opening profiles of such Vickers inden...

Fatigue cracking is one of the most common failure modes of various load-bearing structures. Even though sensors of many different types have been developed for crack detection, very few can monitor crack growth with a high sensitivity. This paper presents an antenna sensor that is capable of monitoring the growth of fatigue cracks with a sub-millimeter resolution. According to microstrip patch...

Fatigue-crack-growth (FCG) rate tests were conducted on compact specimens made of an Inconel-718 alloy to study the behavior over a wide range in load ratios (0.1 6 R 6 0.95) and a constant Kmax test condition. Previous research had indicated that high R (>0.7) and constant Kmax test conditions near threshold conditions were suspected to be crack-closure-free and that any differences were attri...

A nominally at penny-shaped crack is subjected to a static loading. A perturbation method is developed for calculating the stress-intensity factors, based on an asymptotic analysis of the governing hypersingular boundary integral equation for the crack-opening displacement. Comparisons with known exact solutions for an inclined at elliptical crack and for a crack in the shape of a spherical cap...

The plane strain problem of determining strain energy release rate, crack energy, and crack-opening displacement (COD) for a moving Griffith crack at the interface of two dissimilar orthotropic half-planes is considered. The problem is reduced to a pair of singular integral equations of second kind which have finally been solved by using Jacobi polynomials. Graphical plots of the strain energy ...

A model has been developed to predict crack opening and closing behavior for propagating fatigue cracks which undergo significant sliding displacements at crack flanks. Crack surfaces were described statistically by assuming a random distribution of asperity heights and a mean density of asperities and asperity radii. The propagating crack was subdivided into strips, and each strip was treated ...

Edge-notched eccentrically compressed fracture specimens made of aggregate of reduced size are loaded in standard creep test frames. Measurements of the time rate of crack mouth opening in notched concrete specimens subjected to constant load of almost one month duration are reported and analyzed. To reveal the size effect, geometrically similar specimens of four sizes in the ratio I :2:4:8 are...

An experimental investigation dealing with failure characterization of 63/37 soldercopper interfaces is presented. The method of moird interferometry is used for mapping elasto-plastic deformations in bimaterials subjected to predominantly tensile loading. A method for quantifying the fracture parameter--the J-integral--using full-field measurement of crack opening displacements has been develo...

An axi{symmetric problem for a penny{shaped crack bridged by bres is considered. The study is reduced to the analysis of a hy-persingular integral equation with respect to the relative crack{face separation over a circular domain occupied by crack. The special case of a large crack subjected to Mode{I loading is examined. A matched asymptotic expansions technique is used in order to estimate th...

concrete is one of the most widely used materials in construction industry. many large and important structures such as power plants, bridges, dams and buildings employ concrete as main material. propagation of crack is considered one of the main reasons in failure of concrete structures. the process of formation and crack growth is one of the major and complex issues in concrete, because concr...