Resistance to cyclic flexural fatigue failure is an important feature of rotary nickel-titanium (NiTi) instruments. The aim of this study was to evaluate the cyclic flexural fatigue failure resistance of RevoS Shaper Universal rotary NiTi files and to compare it to two other rotary NiTi files with similar size and taper, the Hero Shaper and the ProFile. Fifteen each of Revo-S Shaper Universal, ...

AIM The aim of the present study was to compare the resistance to cyclic fatigue of Hyflex® (Coltene-Whaledent, Allstatten, Switzerland) size 40 taper.04 nickel titanium instruments used in continuous rotation versus the use with a reciprocating motion. The null hypothesis was that different file motions had no influence on the lifetime of instruments subjected to a cyclic fatigue test. METHO...

AIM To compare the cyclic fatigue resistance of new generation OneShape and WaveOne instruments when used with different kinematics. METHODOLOGY An artificial canal, made of stainless steel with an inner diameter of 1.5 mm, a 60° angle of curvature and a curvature radius of 3 mm, was used for cyclic fatigue test of new generation OneShape and WaveOne instruments. Groups were as follows (n = 2...

Statement of the Problem File fracture can interfere with cleaning and shaping of the canal and compromise periradicular healing. Autoclave sterilization may prone the files to fracture. Purpose The purpose of the present study was to determine the effect of autoclave sterilization on the cyclic fatigue resistance of Hero642 rotary instrument in two curvatures of 45 and 60 degrees. Material...

Total strain-controlled low-cycle-fatigue tests with and without hold times were performed at temperatures ranging from 816°C to 982°C in a laboratory air on a nickel-based superalloy, HASTELLOY X. The influence of hold times on the cyclicstress response and fatigue life was studied. At the temperatures considered, the alloy exhibited initial cyclic hardening, followed by a saturated cyclic-str...

Fatigue crack growth has been observed recently in ferroelectrics under cyclic electric loading[ Does the crack grow by electric breakdown\ or by the stress _eld near the crack tip< The present paper provides a mechanistic explanation for the electric!_eld!induced fatigue crack growth[ The non!uniform electric _eld near an insulated crack tip might cause domain switching which in turn produces ...

An evaluation of the fatigue crack resistance of human dentin was conducted to identify the degree of degradation that arises with aging and the dependency on tubule orientation. Fatigue crack growth was achieved in specimens of coronal dentin through application of Mode I cyclic loading and over clinically relevant lengths (0 ≤ a ≤ 2 mm). The study considered two directions of cyclic crack gro...

Objectives It was aimed to compare the cyclic fatigue resistances of ProTaper Universal (PTU), ProTaper Next (PTN), and ProTaper Gold (PTG) and the effects of sterilization by autoclave on the cyclic fatigue life of nickel-titanium (NiTi) instruments. Materials and Methods Eighty PTU, 80 PTN, and 80 PTG were included to the present study. Files were tested in a simulated canal. Each brand of ...