Production of nickel-silver by mechanical alloying was investigated. Effects of parameters such as milling duration, ball to powder weight ratio, and chemical composition on mechanical alloying process, and alloy's color and microstructure were studied. The milled powders were characterized, using XRD and SEM. Results showed that nickel-silvers could be produced by mechanical alloying in a wide...

Production of nickel-silver by mechanical alloying was investigated. Effects of parameters such as milling duration, ball to powder weight ratio, and chemical composition on mechanical alloying process, and alloys color and microstructure were studied. The milled powders were characterized, using XRD and SEM. Results showed that nickel-silvers could be produced by mechanical alloying in a wide ...

in this research, the effect of different biopolymers such as polyethylene glycol (peg) and polyvinylalcohol (pva) on synthesis and characterization of polymer/cobalt ferrite (cf) nano-composites bymechanical alloying method has been systematically investigated. the structural, morphological andmagnetic properties changes during mechanical milling were investigated by x-ray diffraction (xrd),fo...

One of the principal problems with nano-crystalline materials is producing them in quantities and sizes large enough for valid mechanical property evaluation. The purpose of this study was to explore an innovative method for producing nano-crystalline γ-TiAl bulk materials using high energy ball milling and brief secondary processes. Nano-crystalline powder feedstock was produced using a Fritsc...

In this research, formation of nanocrystalline Ni3Al intermetallic from Ni and Al elemental powders by mechanical alloying (MA) process and its characterization was investigated. Therefore, the evolutions in microstructure such as phase transformation, oxidation in air and introduction of Fe impurity from milling media after MA were evaluated using XRD, Rietveld refinement, TEM, SEM, EDS and IC...

Due to the large thermal neutron absorption cross section of 10B, B4C-Al composites have been used as neutron absorbing materials in nuclear industries, which can offer not only good neutron shielding performance but also excellent mechanical properties. The distribution of B4C particles affects the mechanical performance and efficiency of the thermal neutron absorption of the composite materia...

The intensification of leaching of gold from a waste using mechanical activation (milling in water) and mechanochemical activation (milling in thiourea solution) were studied as the pretreatment steps. The leaching of “as-received“ sample in an acid thiourea solution resulted in 78 % Au dissolution, after mechanical activation 98 % and mechanochemical activation up to 99 % of the gold was leach...

The as-synthesized nanowires and nanobelts usually have a large size distribution. We demonstrate here a ball milling technique for narrowing the size distribution of oxide nanobelts and nanowires. High-resolution scanning and transmission electron microscopy reveals that the one-dimensional SnO2 nanostructures with size .150 nm are sensitive to the milling effect and most of them were fracture...

The formation of ZnSe via a mechanically-induced self-sustaining reaction (MSR) from a Zn/Se mixture showed that only size reduction and mixing of the reactants without product formation occurred during the induction period prior to ignition. Therefore, all mechanical energy supplied by the planetary mill during this time, called the ignition time (tig), was used exclusively in the activation o...

The effect of milling on the particle size and mechanical properties Tungsten Carbide - Cobalt composite were investigated. First, raw materials ratios by mechanical milling for 4 hours at 300 rpm were mixed. The powder in the optimum temperature 1350°C at a rate of temperature rise 50°C / min and shelf life of 4 minutes and the pressure MPa 30 were sintered in SPS. The results indicated nearly...