In order to make fast-charging batteries a reality for electric vehicles, durable, more energy dense and high-current density resistant anodes need to be developed. With such purpose, a low lithiation potential of 0.2 V vs. Li/Li(+) for MoO3 nanoplatelet arrays is reported here for anodes in a lithium ion battery. The composite material here presented affords elevated charge capacity while at t...

Molybdenum oxide nitride (denoted as Mo(O,N)3) was obtained by ammonolysis of α-MoO3 with gaseous ammonia. Electronic and geometric structure, reducibility, and conductivity of Mo(O,N)3 were investigated by XRD, XAS, UV-Vis spectroscopy, and impedance measurements. Catalytic performance in selective propene oxidation was determined by online mass spectrometry und gas chromatography. Upon incorp...

The temperature-programmed reduction of MoO3 from 300 K to 773 K in 50 vol-% hydrogen in He (10 Pa) at different heating rates (0.1, 0.2, and 5 K/min) was investigated by in situ XRD and XAFS. At heating rates of ~ 0.1 and ~ 0.2 K/min the formation of the molybdenum bronze H0.34MoO3 was observed by in situ XRD in the early stage of the reduction of MoO3. At a heating rate of 5 K/min the formati...

In situ X-ray absorption spectroscopy (XAS) under reaction conditions of selective propene oxidation was employed to elucidate the local structure of as-prepared and activated molybdenum oxide supported on hollow vapor-grown carbon nanofibers (VGCNF). The local structure of asprepared MoxOy-VGCNF was very similar to that of hexagonal MoO3. During heat treatment in propeneand oxygen-containing a...

Supported early transition metal oxides have important applications in numerous catalytic reactions. In this article, we review the synthesis and activity of well-defined model WO3 and MoO3 catalysts that are prepared via deposition of cyclic gas-phase (WO3)3 and (MoO3)3 clusters generated by sublimation of WO3 and MoO3 powders. Conversion of small aliphatic alcohols to alkenes, aldehydes/keton...

Using a 10 nm thick molybdenum oxide (MoO3-x) layer as a transparent and low barrier contact to p-CdTe, we demonstrate nanowire CdS-CdTe solar cells with a power conversion efficiency of 11% under front side illumination. Annealing the as-deposited MoO3 film in N2 resulted in a reduction of the cell's series resistance, from 9.97 Ω/cm(2) to 7.69 Ω/cm(2), and increase in efficiency from 9.9% to ...

The interface structure of graphene with thermally evaporated metal oxide layers, in particular molybdenum trioxide (MoO3), is studied combining photoemission spectroscopy, sheet resistance measurements and organic light emitting diode (OLED) characterization. Thin (<5 nm) MoO3 layers give rise to an 1.9 eV large interface dipole and a downwards bending of the MoO3 conduction band towards the F...

background; in recent years, nanoparticles have been increasingly used in industries. however, there is a serious lack of information concerning their impact on human health and the environment. this study was investigated the effect of moo3 nps on thyroid hormones in female rats. methods; in this study, 21 female wistar rats were selected and divided into three groups of untreated control, sha...

Molybdenum and zirconium mixed oxides were supported on siliceous MCM-41 mesoporous material. The resultant materials were characterized with various techniques such as X-ray diffraction (XRD), nitrogen adsorption, Transmission electron microscopy (TEM), XANES, NH3-TPD, and Diffuse reflectance infrared Fourier transform spectra (DRIFTS) of pyridine. It was found that the well-ordered channeling...

Fifteen distinct MgO–V2O5, MgO–MoO3, MgO–V2O5–MoO3, and V2O5–MoO3 compositions were prepared using sol–gel chemistry and their selectivities and conversions for propane oxidative dehydrogenation (ODH) to propylene were measured. The vanadates were more active than the molybdates at lower temperatures; however, the molybdates exhibited higher selectivities at similar conversions. An increase in ...