Solidification of pure aluminum without and with a magnetic field has been investigated by differential thermal analysis (DTA). DTA curves showed that the nucleation temperature of pure aluminum was decreased as a magnetic field strength increased although its melting process was almost not influenced. The nucleation suppression could be attributed to the increase of the solidliquid interfacial...

Three types of self-piercing riveting (SPR) joints, i.e., steel/aluminum, carbon fiber reinforced polymer (CFRP)/ aluminum, and aluminum/aluminum, were constructed using three different top sheet materials with the same aluminum alloy as bottom sheet. The effects material on joint quality mechanical behavior evaluated. materials’ characteristics dominate rivet piercing process consequent interl...

The formation of in situ AlN-TiN-TiB2/Al composite inoculants, which contain multi-phase refiner particles including AlN, TiN, TiB2, Al3Ti, and α-Al, was investigated using nitrogen gas injection. The effects of the main preparation parameters such as nitriding temperature, nitriding time, Ti content in melts, on the microstructure and grain refinement of in situ AlN-TiN-TiB2/Al composite inocu...

This paper describes a novel technique for joining similar and dissimilar metal foils, namely micro clinching with cutting by laser shock forming. A series of experiments were conducted to study the deformation behavior of single layer material, during which many important process parameters were determined. The process window of the 1060 pure aluminum foils and annealed copper foils produced b...

Piezoelectric aluminum nitride thin films were deposited on aluminum-molybdenum (AlMo) metallic nanocomposites using reactive DC sputtering at room temperature. The effect of sputtering parameters on film properties was assessed. A comparative study between AlN grown on AlMo and pure aluminum showed an equivalent (002) crystallographic texture. The piezoelectric coefficients were measured to be...

Vapor grown carbon fiber reinforced pure aluminum matrix composites were fabricated by the hot-pressing method below the melting temperature of pure aluminum. The surface structures of the vapor grown carbon fibers and the interfacial structures between the fibers and the matrix in the composite were observed. The precipitation mechanism of crystalline aluminum carbide was also investigated. An...