The method of In bilayer pre-deposition and penetrated nitridation had been proposed, which had been proven to have many advantages theoretically. To study the growth behavior of this method experimentally, various pulse times of trimethylindium supply were used to get the optimal indium bilayer controlling by metalorganic vapour phase epitaxy. The results revealed that the InN film quality bec...

Dense machinable α-SiAlON/BN composites were fabricated by hot-pressing using turbostratic boron nitride (tBN) obtained from nitridation of melamine diborate. The tBN was added to the starting powders, or introduced as a coating that formed in situ on α-Si3N4 carrier powders during nitridation, and was subsequently converted to hexagonal boron nitride (hBN) during hot pressing by solution repre...

We report a synergistic effect involving hydrogenation and nitridation cotreatment of TiO(2) nanowire (NW) arrays that improves the water photo-oxidation performance under visible light illumination. The visible light (>420 nm) photocurrent of the cotreated TiO(2) is 0.16 mA/cm(2) and accounts for 41% of the total photocurrent under simulated AM 1.5 G illumination. Electron paramagnetic resonan...

In this report, self-organized GaN nanodots have been grown on Si (111) by droplet epitaxy method, and their density can be controlled from 1.1 × 10(10) to 1.1 × 10(11) cm(-2) by various growth parameters, such as substrate temperatures for Ga droplet formation, the pre-nitridation treatment of Si substrate, the nitridation duration for GaN crystallization, and in situ annealing after GaN forma...

A nitridation treatment technology with a urea/ammonia complex nitrogen source improved resistive switching property in HfO2-based resistive random access memory (RRAM). The nitridation treatment produced a high performance and reliable device which results in superior endurance (more than 109 cycles) and a self-compliance effect. Thus, the current conduction mechanism changed due to defect pas...

The catalytic effects of chromium (Cr) on the direct nitridation of silicon (Si) and morphology of nitridation product were investigated. Cr dramatically improved the conversation of Si to silicon nitride (Si3N4). The complete conversion was achieved at 1350 °C upon addition of 1.25 wt% Cr. This temperature was much lower than that required in the case without using a catalyst. Meanwhile, Cr pl...

The behavior of alloys in nitrogen at high temperature is relevant to many industrial applications. Embrittlement due to internal nitride formation is the principal problem encountered in service. In this study, the nitridation resistance of a series of alloys in pure nitrogen at 1093 O C was investigated. For Fe-base, Ni-base, and Co-base alloys the amount of nitrogen absorbed and the nature a...

Fe16N2 fine particles were prepared by reduction in 5% H2/Ar gas mixture flow, starting from goethite or hematite precursors, followed by nitridation in ammonia gas flow. Small amounts of metallic iron and iron oxide are present besides the main phase which is an ordered iron nitride having martensite structure (α ’’ -Fe16N2) as revealed by Mössbauer spectroscopy measurements. However, X-ray di...

Gallium nitride (GaN) nanopowder used as a blue fluorescent material was synthesized by using a direct current (DC) non-transferred arc plasma. Gallium nitrate hydrate (Ga(NO₃)₃∙xH₂O) was used as a raw material and NH₃ gas was used as a nitridation source. Additionally, melamine (C₃H₆N₆) powder was injected into the plasma flame to prevent the oxidation of gallium to gallium oxide (Ga₂O₃). Argo...

In turbine engines, high temperature components made of superalloys may crack in a creep process during service. With the inward flux of the gases, e.g. oxygen and nitrogen, along those cracks, the microstructure of the superalloy substrate nearby the cracks may degrade by internal oxidation and nitridation. The aim of this study is to investigate and simulate the oxidation-nitridation-induced ...