Steel composites reinforced with alumina nanoparticles were prepared by powder metallurgy process. Samples containing two different amounts of carbon (0.35 and 0.55 wt.%) and 0-5 wt.% Al2O3 nanoparticles were fabricated by mixing, compacting and sintering of diffusion bonded Distaloy AE powder. The density, hardness and wear tests were performed on the prepared samples. Fu...

Bimetallic parts are used in many industries for weight and cost reduction of workpieces working under high loads and wear. One application for this type of composite material is in automotive industry. In this work the tool wear and cutting forces in the face milling of bimetallic parts made of aluminum and cast iron were investigated. A356 and GG25 alloys that are common materials for bimetal...

In this paper, the wear resistance and antifriction of epsilon phase layer and diffusion layer of gas nitrided D2 steel and M2 steel have been studied. The changes m wear mechanism of epsilon phase under the load from 20N to 200N are analysed. When the load is lighter than 100N, it is mainly oxidizing wear on friction surface. The adhesion, peeling off and abrasive wear appear on friction surfa...

conclusions estelite sigma quick composite had wear resistance similar to that of nano- and microfilled composites. estelite flowable composites demonstrated similar wear resistance to that of a posterior composite. results the wear amounts of the composites are as follows in order: estelite sigma quick (1886.9 ± 518.5 μm2), estelite flow quick (2708.9 ± 578.1 μm2), estelite high flow (3206 ± 2...

in this research, our attempt is to monitor tool wear through the chip formations, forces, and temperature of edge of drill while drilling in superalloy plate to optimizes effective parameters, which lead to facilitate machining process to, improved tool life, and enhance the productivity. in this study, inconel718 superalloy material, and cemented coated carbide tool was selected for investiga...

The wear mechanism of plasma electrolytic nitrocarburised (PEN/C) 316L stainless steel samples was studied after a pin on disc wear test. The surface morphology of samples after application of PEN/C process was studied using scanning electron microscope technique. The sliding tracks resulting from the wear tests on the treated specimens indicated no signs of plastic deformation and adhesive wea...

in this work, homogeneous thermochemical co-precipitation method was used to fabricate w-25wt%cu nanocomposite. synthesized nanocomposite powder was calcined and reduced. a hydrogen atmosphere sintering at 1200oc for 105 consolidated the product up to a density close to 98% theoretical density. wear experiment were carried out using a pin-ondisc set up at three normal loads of 5, 10 and 15 n an...