Bulk crystals of ZnS usually take the zinc blende structure. However, the vapor deposited one-dimensional ZnS nanostructures normally take the metastable wurtzite structure. This Letter investigates the conditions under which the formed phase can be controlled between zinc blende and wurtzite in nanomaterials synthesis. The formation of pure zinc blende structured ZnS nanobelts is related not o...

A kinetic study of vinyl acetate (VA) synthesis over a Pd(100) catalyst is described, and the effect of particle-size on this reaction ascertained by comparing the single crystal data with data from supported Pd catalysts (5 wt% Pd/SiO2, dPd=4.2 nm, and 1 wt% Pd/SiO2, dPd=2.5 nm). A negative reaction order with respect to ethylene and a positive order with respect to oxygen were found for the m...

dissolution pressure and nozzle temperature effects on particle size and distribution were investigated for ress (rapid expansion of supercritical solution) process. supercritical co2 was used as solvent and ibuprofen was applied as the model component in all runs. the resulting ibuprofen nano-particles (about 50 nm in optimized runs) were analyzed by sem and laser diffraction particle size ana...

A novel Mo-promoted Ce-Zr mixed oxide catalyst prepared by a homogeneous precipitation method was used for the selective catalytic reduction (SCR) of NO(x) with NH3. The optimal catalyst showed high NH3-SCR activity, SO2/H2O durability, and thermal stability under test conditions. The addition of Mo inhibited growth of the CeO2 particle size, improved the redox ability, and increased the amount...

A weak surface modification is applied to Co/SiO2 catalyst by hydrothermal treatment at 180°C for 5 h. Aluminum is introduced to Co/SiO2 catalysts during the surface modification. The effects of surface modification on Co/SiO2 catalyst are studied by changing the operating sequences of surface modification and cobalt impregnation in the catalyst preparation. Surface modification before cobalt i...

the nanoparticles of ni–si mixed oxides were prepared by co-precipitation method using nickel nitrate; ni(no3)2 6h2o and tetraethylorthosilicate (teos). the products were characterized by x-ray diffraction (xrd), transmission electron microscopy (tem), and hydrogen temperature program reduction (h2-tpr). the results revealed that ni–si mixed oxides particles were obtained with average particle ...

TiO(2) porous nanospheres on polypropylene (PP) films (TiO(2)/PP composite) are produced at ambient temperature. Particle/pore size match up is the key anchoring point to overcome the low affinity between hydrophilic materials and hydrophobic materials. With the hydrophilic TiO(2) catalyst evenly dispersed on a hydrophobic surface, the aqueous solution will selectively skip the substrate and we...

In this study simple catalytic test experiment was performed in a flask of rotary evaporator for dechlorination of nitrochlorobenzene (NCB) over two samples of Ni/LaAl2 O3 nanocatalysts (C1 and C2). In the reaction, Ni acts as a catalyst to collect hydrogen gas in aqueous solution and dissociate it to produce active hydrogen atoms for replacing the chlorine. The catalysts were characterized by ...

Ag-based catalysts with different supports (TiO2, Al2O3 and CeO2) were prepared by impregnation method and subsequently tested for the catalytic oxidation of formaldehyde (HCHO) at low temperature. The Ag/TiO2 catalyst showed the distinctive catalytic performance, achieving the complete HCHO conversion at around 95 °C. In contrast, the Ag/Al2O3 and Ag/CeO2 catalysts displayed much lower activit...