The wear resistance of microfilled and conventional composite resins, was examined, using two sizes of abrasive particles for polishing. The mechanical properties of the composite resins were also studied and evaluated in relation to wear. Conventional composites showed much lower wear resistance than the microfilled resins. The amalgam and human enamel abraded with 10ƒÊm SiC particles, had str...
The purpose of this study was to evaluate the effect of polishing procedures on the color stability of different types of composites after aging. Forty disk-shaped specimens (Ø10×2 mm) were prepared for each composite resin type (an ormocer, a packable, a nanohybrid, and a microhybrid) for a total of 160 specimens. Each composite group was divided into four subgroups according to polishing meth...
The intimate marginal adaptation of composite resins is considered to be the most important requisite, and this is strongly influenced by polymerization shrinkage, thermal expansion or mechanical properties of the resins. The highly loaded composite resins, developed recently have yielded good results on thermal expansion and mechanical properties. Consequently, little attention has been paid t...
The use of dental acrylics and composite resins in veterinary dentistry has become widespread. However their use is not without potential complications. All acrylics and composite resins produce an exothermic reaction during the polymerization process. The aim of the current study was to evaluate thermal conduction during the polymerization reaction of each material to offer clinical guidelines...
The relationship between the wear of three composite resins and the hardness of the abrasive was studied by a two-body abrasion test. The wear rates of the composites increased linearly with abrasive hardness from 530 to 2080 KHN. Measurement of the slope of the wear rate versus abrasive hardness over this range provided a sensitive method for ranking the composites.
The surface degradation of composite resins caused by accelerated aging was studied. Accelerated aging for 900 hours caused erosion of the resin matrices and exposure of filler particles. Differences in surface profiles after aging suggest that the materials eroded at different rates. Accelerated aging may model erosive wear of composites.
The aim of this study was to evaluate the fluorescence intensity of different composite resins and compare those values with the fluorescence intensity of dental tissues. Different composite resins were used to make 10 discs (2 mm in depth and 4 mm in diameter) of each brand, divided into groups: 1) Z (Filtek Z350, 3M ESPE), 2) ES (Esthet-X, Dentsply), 3) A (Amelogen Plus, Ultradent), 4) DVS (D...
OBJECTIVES This study was performed to determine whether the combined use of one-bottle self-etch adhesives and composite resins from same manufacturers have better bond strengths than combinations of adhesive and resins from different manufacturers. MATERIALS AND METHODS 25 experimental micro-shear bond test groups were made from combinations of five dentin adhesives and five composite resin...
To evaluate the ultimate compressive strength of five composite resins after 1 hour, 24 hours, 7 days and 1 month. Twenty four cylindric...