This work addresses two transitions in material behavior: one, the initial peak in stress response associated with dynamic recrystallization and two, the rapid increase in grain growth rate associated with pore separation from grain boundaries. A criterion is derived that predicts the initial peak in stress response associated with dynamic recrystallization, and another criterion is derived tha...

Recrystallization in copper deformed by dynamic plastic deformation was investigated using electron backscatter diffraction. The recrystallized grains show a broad size distribution. The kinetics of grains of different sizes is observed to be different: In the beginning of recrystallization, the area fraction of small recrystallized grains increases rapidly. At later stages of recrystallization...

An AM30 magnesium alloy was processed through ECAP method at 200 °C. Optical and transmission electron microscopy as well as electron back scattered diffraction (EBSD) technique were employed to characterize the deformed microstructure. A partially recrystallized microstructure including ultrafine/nano structures was obtained. The area fraction of 49% was measured for the recrystallized regions...

Friction stir processing (FSP) was conducted on a SAF 2205 duplex stainless steel at advancing speed of 50 mm/min and rotational speed of 400 rpm.  Characterization of evolved material was studied using electron microscopy equipped with electron back scattered diffraction (EBSD) system. The results indicated that the severe plastic deformation and the heat generated during the FSP developed a v...