Aircraft turbine engines routinely experience the ingestion of debris resulting in “foreign object damage” or FOD. Failures associated with foreign object damage have been estimated to cost the aerospace industry $4 billion per year. Often, FOD does not lead to sudden catastrophic failure, yet such damage can dramatically reduce the lifetime of components subjected to cyclic fatigue stresses. T...

Fatigue life prediction and evaluation are the key technologies to assure the safety and reliability of automotive rubber components. The objective of this study is to develop the fatigue analysis process for vulcanized rubber components, which is applicable to predict fatigue life at initial product design step. Fatigue life prediction methodology of vulcanized natural rubber was proposed by i...

This paper addresses the contribution, or otherwise, of fatigue to personal damage on mining sites in Australia. It does not address personal damage involving travel to work or off-site road accidents e.g. transport of equipment to and from sites. The story which would be told with respect to fatigue and its contribution to traffic accidents in the public sector would be quite different to that...

Miniaturisation of electronic products is increasingly important for reasons of functionality enhancement and freedom of design. This is realised by integration into silicon and developing miniature packages with high I/O and power dissipation density. Generally this leads to elevated temperatures, not only in the components but also in the solder joints. Elevated temperature cycling leads to f...

High cycle fatigue has become the leading cause of failure in gas turbine engine blades in recent years [1]. The majority of these failures were associated with surface damage such as foreign object damage (FOD). Therefore, the ability of a material to resist impact damage and the subsequent fatigue propagation of any cracks that may result has become a crucial design consideration. Substantial...

The fatigue fracture of a drillstring could cause drilling disturbances and some negative impacts (e.g., economic loss) will be brought when restoring the drillstring to functionality. In order to evaluate the effects of the fatigue damage of the drillstring during drilling, a new apparatus, which could monitor the load level in real-time, was built to perform the four-point bending fatigue tes...

In this paper, the fatigue damage and lifetime of 2D SiC/SiC ceramic-matrix composites (CMCs) under cyclic fatigue loading at 750, 1000, 1100, 1200 and 1300 °C in air and in steam atmosphere have been investigated. The damage evolution versus applied cycles of 2D SiC/SiC composites were analyzed using fatigue hysteresis dissipated energy, fatigue hysteresis modulus, fatigue peak strain and inte...

Cables play an important role in cable-stayed systems, but are vulnerable to corrosion and fatigue damage. There is a dearth of studies on the fatigue damage evolution of corroded cable. In the present study, the acoustic emission (AE) technology is adopted to monitor the fatigue damage evolution process. First, the relationship between stress and strain is determined through a tensile test for...

Commercial transport aircraft are required to operate under the concept of damage tolerance. Because of the structural redundancy and the crack arrest capability, the current fleet of commercial aircraft was initially designed to have sufficient residual strength to sustain discrete source damage. However, fatigue damage during the life of an aircraft can significantly reduce the residual stren...

A general methodology for stochastic fatigue life prediction under variable amplitude loading is proposed in this paper. The methodology combines a nonlinear fatigue damage accumulation rule and a stochastic S–N curve representation technique to achieve this objective. The nonlinear damage accumulation rule proposed in this paper improves the deficiencies inherent in the linear damage accumulat...