With the increases in work environment regulations restricting alcohol to 1000 ppm, and drink-driving laws, testing for with a simple method is crucial issue. Conventional sensors based on sulfide, metal oxide, boron nitride or graphene oxide have detection limit range of 50–1000 ppm but disadvantages complicated manufacture longer processing times. A recent portable meter semiconductor materia...

Nanochannel arrays were fabricated by the self-organized multi-electrolyte-step anodic aluminum oxide [AAO] method in this study. The anodization conditions used in the multi-electrolyte-step AAO method included a phosphoric acid solution as the electrolyte and an applied high voltage. There was a change in the phosphoric acid by the oxalic acid solution as the electrolyte and the applied low v...

The self-ordering of nanoporous anodic aluminum oxide (AAO) in the course of the hard anodization (HA) of aluminum in sulfuric acid (H2SO4) solutions at anodization voltages ranging from 27 to 80 V was investigated. Direct H2SO4-HA yielded AAOs with hexagonal pore arrays having interpore distances D(int) ranging from 72 to 145 nm. However, the AAOs were mechanically unstable and cracks formed a...

Thin films of porous anodic aluminum oxide (AAO) on tin-doped indium oxide (ITO) substrates were fabricated through evaporation of a 1,000- to 2,000-nm-thick Al, followed by anodization with different durations, electrolytes, and pore widening. A faster method to obtain AAO on ITO substrates has been developed, which with 2.5 vol.% phosphoric acid at a voltage of 195 V at 269 K. It was found th...

This paper aims to fabricated high quality anodic aluminum oxide (AAO) film by anodization method. AAO pore size, pore density, and film thickness can be controlled in 10~500 nm, 10~10 pore.cm, and 1~100 μm. AAO volume and surface area can be computed based on structural parameters such as thickness, pore size, pore density, and sample size. Base on the thetorical calculation, AAO has 100 μm th...

Dielectric capacitors are promising candidates for high-performance energy storage systems due to their high power density and increasing energy density. However, the traditional approach strategies to enhance the performance of dielectric capacitors cannot simultaneously achieve large capacitance and high breakdown voltage. We demonstrate that such limitations can be overcome by using a comple...

Citation: Iglesias L, Vega V, García J, Hernando B and Prida VM (2015) Development of electrostatic supercapacitors by atomic layer deposition on nanoporous anodic aluminum oxides for energy harvesting applications. Front. Phys. 3:12. doi: 10.3389/fphy.2015.00012 Development of electrostatic supercapacitors by atomic layer deposition on nanoporous anodic aluminum oxides for energy harvesting ap...

Plasma sputtering deposition of Platinum thin films is studied on porous anodic aluminum oxide (AAO) template. The size effect of AAO cylindrical pores is shown to influence the diffusion of atoms in the porous layer. The resulting maximum reached depth of platinum varied from 2 μm to 20 μm, and the density on the surface is lowered from 23 μg.cm to 5 μg.cm as the pore diameter increased from 4...

Bismuth oxychloride (BiOCl) nanowire arrays have been successfully prepared employing the Anodic Aluminum Oxide (AAO) template assisted sol-gel method. Nanowires of 100 nm diameter and length 26 μm, assembled in the porous of AAO templates, were formed. XRD and HRTEM results show that the nanowires are pure BiOCl polycrystal phase without Bi2O3 or BiCl3. The photocatalytic activity of BiOCl nan...

Anodic aluminum oxide (AAO) templates are used to fabricate arrays of poly(3-hexylthiophene) (P3HT) pillars. This technique makes it possible to control the dimensions of the pillars, namely their diameters, intervals, and heights, on a tens-of-nanometer scale. These features are essential for enhancing carrier processes such as carrier generation, exciton diffusion, and carrier dissociation an...