In laser forming, phase transformations in the heat-affected zone take place under steep thermal cycles, and have a significant effect on the flow behavior of Ti–6Al–4V alloy and the laser-forming process. The flow-stress data of a material are generally provided as only dependent on strain, strain rate, and temperature, while phase transformations are determined by both temperature and tempera...

This paper presents investigations on turning Ti–6Al–4V alloy withmulti-layer coated inserts. Turning of Ti–6Al–4V using uncoated, TiAlN coated, and TiAlN + cBN coated single and multi-layer coated tungsten carbide inserts is conducted, forces and tool wear aremeasured. 3D finite elementmodelling is utilized to predict chip formation, forces, temperatures and tool wear on these inserts. Modifie...

The effect of the ultrasonic surface rolling process (USRP) on the rotary bending fretting fatigue (FF) of Ti-6Al-4V alloy was investigated. The reason for the USRP's ability to improve the FF resistance of Ti-6Al-4V alloy was studied. The results revealed that the USRP induced a compressive residual stress field with a depth of 530 μm and a maximum residual stress of -930 MPa. Moreover, the su...

ti-6al-4v titanium alloy has great application in medicine and military industries due to its capabilities, namely high strength to weight ratio and corrosion resistance. in the current research, the effect of aging treatment on microstructure and wear behavior of ti-6al-4v titanium alloy was investigated. pin on disk wear test was applied to assess the wear behavior. specimens were first solut...

The current work deals with the analysis of mechanisms involved during the machining process of titanium alloys. Two different materials were chosen for the study: Ti-6Al-4V and Ti-55531. The objective was to understand the effect of all cutting parameters on the tool wear behavior and stability of the cutting process. The investigations were focused on the mechanisms of the chip formation proc...

The diamond-like carbon (DLC) films deposited on the articulating surface of medical-grade Ti and Ti–6Al–4V were characterized. The DLC films were synthesized by r.f. plasma assisted chemical vapor deposition (PACVD) using C6H6 at 10 mTorr. For wear tests, the ball-ondisk type wear tester was employed by wearing a 5-mm diameter ruby ball against a rotating metal disk. The DLC coating dramatical...

In this paper, a nanocrystalline surface layer without impurities was fabricated on Ti-6Al-4V alloy by means of surface mechanical attrition treatment (SMAT). The grain size in the nanocrystalline layer is about 10 nm and grain morphology displays a random crystallographic orientation distribution. Subsequently, the low-temperature boriding behaviors (at 600 °C) of the SMAT sample, including th...

Ti-6Al-4V alloy is the most commonly used alloy for dental and orthopedic implants. In order to improve osseointegration, different surface modification methods are usually employed, including self-assembled monolayers (SAMs). This study presents an investigation of both active (electroassisted) and passive (adsorption) approaches for the modification of Ti-6Al-4V using alkylphosphonic acid. Th...

This paper presents some examples of knee and hip implant components containing porous structures and fabricated in monolithic forms utilizing electron beam melting (EBM). In addition, utilizing stiffness or relative stiffness versus relative density design plots for open-cellular structures (mesh and foam components) of Ti-6Al-4V and Co-29Cr-6Mo alloy fabricated by EBM, it is demonstrated that...

The in situ tensile straining of cross-sectional specimens inside a TEM is intrinsically very difficult to perform despite its obvious interest to study interfaces of surface treated materials. We have combined a FIB-based method to produce H-bar specimens of a nitrided Ti-6Al-4V alloy and in situ TEM straining stage, to successfully study the plastic deformation mechanisms that are activated c...