Ultrafine-grained pure titanium prepared by equal-channel angular pressing has favorable mechanical performance and does not contain alloy elements that are toxic to the human body. It has potential clinical value in applications such as cardiac valve prostheses, vascular stents, and hip prostheses. To overcome the material's inherent thrombogenicity, surface-coating modification is a crucial p...

Grain refinement can make conventional metals several times stronger, but this comes at dramatic loss of ductility. Here we report a heterogeneous lamella structure in Ti produced by asymmetric rolling and partial recrystallization that can produce an unprecedented property combination: as strong as ultrafine-grained metal and at the same time as ductile as conventional coarse-grained metal. It...

Accumulative roll-bonding process (ARB) is an important severe plastic deformation technique for production of the ultrafine grained, nanostructured and nanocomposite materials in the form of plates and sheets. In the present work, this process used for manufacturing Al/SiO 2 nanocomposites by using Aluminum 1050 alloy sheets and nano sized SiO 2 particles, at ambient temperature. After 8 cycle...

This work has two primary goals. The first is to advance our fundamental understanding of grain boundaries by making direct measurements of grain boundary thermodynamic properties using ultrafine-grained materials. The second is to explore possible deviations from conventional behavior at ultrafine grain sizes, specifically in regards to grain boundary thermodynamic properties and solute segreg...

A microstructure consisting of ultrafine grained (UFG) ferrite with average grain size of ~ 0.7 µm and dispersed nano-sized carbides was produced by cold-rolling and tempering of the martensite starting microstructure in a low carbon steel. Subsequently, fine grained dual phase (DP) steel consisting of equiaxed ferrite grains with average size of ~ 5 µm and martensite islands with average size ...

9 = 0.6 I / s ' 7 = 6.0 0 7 = 2 4 i ti 3 = 6 0 Through close control over green-state powder processing, pure alumina ceramics of 0.5-pm grain size were obtained by sintering at 1250°C. The static grain growth of this material was modest at temperatures below 1300°C. However, dynamic grain growth occurred rapidly during superplastic deformation. Therefore, although the ultrafine-grained alumina...