In this work the effects of WC concentration on abrasive wear behavior by thermally sprayed WC coating was evaluated using three body abrasive wear tester. A different combination of WC and NI coatings were deposited on steel substrates by flame spraying using powder with different WC concentrations (0 %, 12.5 %, 25 %, and 50 %). Flame torch was used for heating and coating of process. Microstr...

In this study, functionally graded Ni-Al2O3 composite coating (FGN-A) has been produced from nickel Watt’s bath containing different concentrations of Al2O3 particles. For this, different composite coatings were electroplated in the same bath with different particles concentration to find the optimum concentration of particles in which the maximum content with uniform distribution of Al2O3 part...

This paper presents the results of testing a wear-resistant ceramic coating on work surface an internal combustion engine (ICE) cylinder’s sleeve. A combined formation technology is described that consists in applying aluminum layer to sleeve’s face by gas dynamic spraying and then covering this with microarc oxidation (MAO). tenfold reduction reinforced sleeve has been determined accelerated c...

Hard coatings have been adopted in cutting and forming applications for nearly two decades. The major purpose of using hard coatings is to reduce the friction coefficient between contact surfaces, to increase strength, toughness and anti-wear performance of working tools and molds, and then to obtain a smooth work surface and an increase in service life of tools and molds. In this report, we de...

The diamond-like carbon (DLC) films deposited on the articulating surface of medical-grade Ti and Ti–6Al–4V were characterized. The DLC films were synthesized by r.f. plasma assisted chemical vapor deposition (PACVD) using C6H6 at 10 mTorr. For wear tests, the ball-ondisk type wear tester was employed by wearing a 5-mm diameter ruby ball against a rotating metal disk. The DLC coating dramatical...

The microstructure and wear resistance of Stellite 6 alloy hardfacing layer at two different temperatures (room temperature and 300°C) were investigated by plasma arc surfacing processes on Q235 Steel. Tribological test was conducted to characterize the wear property. The microstructure of Stellite 6 alloy coating mainly consists of α-Co and (Cr, Fe)7C3 phases. The friction coefficient of Stell...

High-entropy alloys (HEAs) are promising structural materials due to their excellent comprehensive performances. The use of mechanically alloyed powders to deposit HEA coatings through atmospheric plasma spraying (APS) is an effective approach that can broaden the application areas of the HEAs. In this paper, a ductility-brittleness AlCoCrFeNiSi system was chosen as an object of study, and the ...

In aviation, the relative sliding between titanium alloy components causes varying degrees of wear. This work aimed at reducing abrasion parts and improving their service life. Three different Ni-based coatings, WC-10Ni, Ni45, NiCr are sprayed on surface Ti6Al4V by HVOF. Test results mechanical tribological properties such coatings show that hardness Ni45 673 HV0.1 438 HV0.1, respectively, whic...

Chromium oxide coatings are chemically inert, have high mechanical strength, hardness and good optical characteristics; therefore, they have been widely used in many applications including corrosion protection, wear resistance, electronics, and optics. Cr2O3 is well suited for wear resistance applications, as it is one of the hardest oxides with 29.5 GPa hardness. Several deposition techniques ...