In recent years, 3 mol% yttria-stabilized tetragonal zirconia polycrystals (3Y-TZP) doped with copper oxide has obtained increasing interest due to its enhanced superplastisity and good potential in tribological applications. In this work, the effect of addition of small amounts (0.8 mol%) of copper oxide on the sintering behavior of 3Y-TZP was studied using a dilatometer and high-temperature X...
In the present study, a tough tetragonal zirconia polycrystalline (Y-TZP) material was developed for use in high-speed infrared windows and domes. The influence of the preparation procedure and the microstructure on the material's optical properties was evaluated by SEM and FT-IR spectroscopy. It was revealed that a high transmittance up to 77% in the three- to five-micrometer IR region could b...
Y-TZP, Ce-TZP and Ce-TZP/Al2O3 materials are widely investigated in dentistry. Digital Light Processing (DLP) is considered as a breakthrough technology for the dental field to fine print Y-TZP green parts. High loading photocurable formulations (>45 vol%) with commercial powders Ce-TZP/30 vol% Al2O3 as-synthesized powder suitable DLP printing were achieved this study. A low specific surface ar...
Introduction: Various surface treatments have been used to improve the adhesion of resin cement to zirconia restorations. The present study aimed to investigate the effects of different surface treatments on the bond strength of resin cement to zirconia (Y-TZP) in clinical practice. Methods: thirty square Y-TZP samples were classified into three groups of 10, including group SB (50 µm sandblast...
Although titanium remains as the prevalent material in dental implant manufacturing new zirconia-based materials that overcome the major drawbacks of the standard 3Y-yttria partially-stabilized zirconia (Y-TZP) are now emerging. In this study, a new ceramic nanocomposite made of alumina and ceria-stabilized TZP (ZCe-A) has been used to produce dental implants with the mechanic and topographic c...
Yttria-stabilized tetragonal zirconia polycrystals (Y-TZP) have proved to be important structural ceramics. High strength and fracture toughness make them attractive candidates for a number of demanding applications. It was established that these advantageous properties are strongly influenced by the ceramic microstructure [1]. The relationships between microstructure and mechanical properties ...
The effects of CeO2 addition on the sintering behavior and mechanical properties of Y-TZP have been investigated over a wide sintering regime by pressureless sintering. It has been revealed that small additions of CeO2 (0.3-1.0 wt%) to Y-TZP were beneficial in enhancing the mechanical properties and hydrothermal ageing resistance of Y-TZP. Sintered samples were used to evaluate the bulk density...
WC/Y–TZP–Al2O3 hybrid ceramic–matrix composites (CMCs) with dispersed Hadfield steel particles were sintered and then tested at sliding speeds in the range of 7–37 m/s contact pressure 5 MPa. Fast low-temperature sinter-forging allowed obtaining micron-sized WC grains, submicron-sized alumina-reinforced yttria partially stabilized polycrystalline tetragonal zirconia (Y–TZP–Al2O3), evenly distri...
background. the color masking ability of a restoration plays a significant role in coveringa discolored substructure; how-ever, this optical property of zirconia ceramics has not been clearly determined yet. the aim of this in vitro study was to evaluate the color masking ability of a zirconia ceramic on substrates with different values. methods. ten zirconia disk specimens,0.5 mm in thickness ...