This paper covers one of the building blocks required to complete a mechanistic CO2 / H2S corrosion model: electrochemistry of carbon steel CO2 corrosion in the presence of traces of H2S (3-250 ppm in the gas phase). Electrochemical impedance spectroscopy and linear polarisation resistance were used to investigate the mechanism of CO2/H2S corrosion in a glass cell at room temperature, at atmosp...

The corrosion behavior of mild steel in the presence of acetic acid (CH3COOH) and carbon dioxide (CO2) has been investigated using electrochemical techniques and weight-loss measurements. Electrochemical measurements have shown that the presence of acetic acid affects predominantly the cathodic reaction. The acetic acid effect is much more pronounced at elevated temperatures when catastrophic c...

Organic corrosion inhibitor is one of lower cost technologies that limit the deterioration of concrete structures. The influence of a newly prepared organic corrosion inhibitor on the corrosion behavior of carbon steel in simulated concrete pore solution was investigated by polarization curves, electrochemical impedance spectroscopy, and so on. The effect of organic corrosion inhibitors on conc...

One of the heaviest problems of reinforced concrete structures consists in the steel armature corrosion. The steel armature condition affects, above all, the properties of horizontal structures. It is to be noted that the corrosion process itself may not be observable from the outside in many cases. This is why studies of non-destructive methods allowing the researchers to detect the degree of ...

Eighteen Kuntscher-type intramedullary rods were obtained after human implantation periods ranging from 1 to 23 years. A clinical evaluation, metallurgical and chemical analyses of each implant were performed. Idiopathic, implant-related pain was the most common reason for removal, but was not related to extent of implant corrosion. When classified as early versus contemporary material compo...

Nowadays, magnesia carbon refractories are very important for the iron and steel industries. It is due to their unique properties, such as low wet ability with melt iron and steel. Therefore, it is important to extend the life of the refractory. In this research, the effect of calcined alumina and nano carbon on mechanical strength and corrosion resistance against slag in magnesia carbon refrac...

To study the durability of shield tunnel concrete segment under coupling multi-factors, the durability and degradation law of reinforced concrete segments under the joint action of carbonation, sulfate, chloride salt and stray current was studied by accelerated environmental and direct current (DC) power simulation test. The results show that the presence of the stray current not only accelerat...

The state-of-the-art in modelling of internal corrosion of oil and gas pipelines made from carbon steel is reviewed. The review covers the effects of: electrochemistry, water chemistry, formation of protective scales and scales, temperature, flow, steel, inhibition, water condensation, glycol/methanol and localized attack. Various mathematical modelling strategies are discussed. 2007 Elsevier L...

Corrosion of 1020 carbon steel coupons in natural seawater over a 1-year period was more aggressive under strictly anaerobic stagnant conditions than under aerobic stagnant conditions as measured by weight loss and instantaneous corrosion rate (polarization resistance). Under oxygenated conditions, a two-tiered oxide layer of lepidocrocite/goethite formed. The inner layer was extremely tenaciou...

Non-corrosive, carbon-based materials are usually used as anodes in microbial fuel cells (MFCs). In some cases, however, metals have been used that can corrode (e.g. copper) or that are corrosion resistant (e.g. stainless steel, SS). Corrosion could increase current through galvanic (abiotic) current production or by increasing exposed surface area, or decrease current due to generation of toxi...