In this study, corrosion behaviour of A356-10 vol.% SiC composites casted by gravity and squeeze casting is evaluated. For this purpose, prepared samples were immersed in HCl solution for 1h at open circuit potential. Tafel polarization and electrochemical impedance spectroscopy (EIS) were carried out to study the corrosion resistance of composites. The Tafel polarization and EIS studies of ...

The electrochemical corrosion behavior of a silver-plated circuit board (PCB-ImAg) in a polluted marine atmosphere environment (Qingdao in China) is studied through a simulated experiment. The morphologies of PCB-ImAg show some micropores on the surface that act as the corrosion-active points in the tests. Cl- mainly induces microporous corrosion, whereas SO₂ causes general corrosion. Notably, ...

Corrosion of reinforcement is one of the main durability problems of concrete structures. The corrosion induces several structural damages which affect the serviceability and the safety of concrete structures. The structural risk is promoting the possibility of embeded sensors which could give alerts in order to repair the structure before reaching dangerous levels of damage. There are an incre...

  Objective: Corrosion resistance is among the most important properties of metal alloys used in the oral cavity. Consumption of acidic foods reduces the salivary pH and intensifies the corrosion of brackets and orthodontic wires. This study aimed to compare electro galvanic corrosion of different orthodontic brackets and wires and determine the amount of ions released into acidic artifici...

In recent years, the corrosion of steel reinforcement has become a major problem in the construction industry. Therefore, much attention has been given to developing methods of predicting the service life of reinforced concrete structures. The progress of corrosion cannot be visually assessed until a crack or a delamination appears. The corrosion process can be tracked using several electrochem...

Abstract: The risks of alternating current (AC) corrosion and overprotection increasingly demand new criteria forcathodically protected pipelines. To assess the risk of AC corrosion, new cathodic protection (CP) criteria have beenproposed based on DC/AC current densities measurements using coupons. The monitoring system designed for thisproject was based on the instant-off method, with steel co...

AIM The aim of the study is to investigate the galvanic corrosion potential of metal injection molding (MIM) brackets to that of conventional brackets under similar in vitro conditions with nickel-titanium and copper nickel-titanium archwires. MATERIALS AND METHODS Twenty-five maxillary premolar MIM stainless steel brackets and 25 conventional stainless steel brackets and archwires, 0.16 inch...