The initial stage of fretting fatigue crack growth is significantly influenced by tangential force induced by fretting action along the contact surface where a mixed-mode crack growth is involved. Fretting crack behavior of aluminum alloy 2024 was studied, taking into account the problem of contact asperities. Finite element was used for the determination of the stress field near the contact su...

This work aims at investigating experimentally fretting corrosion, that is, corrosion induced by friction of AISI 316L SS against poly(methyl methacrylate) under small displacements, and subsequently using the data to model wear. The observed wear on the stainless steel has been modeled using the Point Defect Model (PDM). The originality of this approach in applying the PDM to fretting corrosio...

This paper presents experimental results of wear process under dry and boundary lubricated metallic (AISI 1034/AISI 52100) contacting bodies with different surfaces morphologies subjected to a wide range of kinematic fretting conditions. Analysis of damage mode observed under such fretting conditions is elucidated in context of surfaces morphologies therefore associated with surface manufacturi...

Fretting fatigue induced by combined localized cyclic contact motion and external bulk fatigue loadings may result in premature and dramatic failure of the contacting components. Depending on fretting and fatigue loading conditions, crack nucleation and possibly crack propagation can be activated. This paper proposes a procedure for estimating these two damage thresholds. The crack nucleation b...

This article describes fretting behavior of zirconia and silicon nitride balls on an electro-deposited coating. Fretting tests are performed using a ball-on-flat configuration. The evolution of the kinetic friction coefficient is determined, along with slip ratio. Experimental results show that the steady-state friction coefficient between ceramic balls (Si₃N₄ and ZrO₂) and an electro-deposited...

The surface characteristics of the contact zone of tin-plated copper alloy contacts subjected to fretting motion for 8000, 16,800 and 48,000 cycles under unlubricated conditions are presented. The nature of the contact zone, at the verge of wearing out of the tin coating as well as upon the coating is completely worn out, is assessed using scanning electron microscopy (SEM), energy-dispersive X...

Fretting corrosion at the taper interface of modular hip implants has been implicated as a possible cause of implant failure. This study was set up to gain more insight in the taper mechanics that lead to fretting corrosion. The objectives of this study therefore were (1) to select experimental loading conditions to reproduce clinically relevant fretting corrosion features observed in retrieved...

Knee and hip joint replacement implants involve a sliding contact between the femoral component and the tibial or acetabular component immersed in body fluids, thus making the metallic parts susceptible to tribocorrosion. Micro-motions occur at points of fixation leading to debris and ion release by fretting corrosion. β-Titanium alloys are potential biomaterials for joint prostheses due to the...

This paper investigates the effect of contact geometry, temperature and displacement amplitude on the fretting behaviour of an aero-turbo oil lubricated cylinder-on-flat contact. To be effective, the lubricant needed both to penetrate the contact and then offer protection. Lubricant penetration into the fretting contact is found to be controlled by two physical parameters, namely (i) the width ...

This paper aims to characterize the surface damage as a consequence of fretting fatigue in aluminum alloy 7075-T6 plates in double-lap bolted joints through XRD, surface profilometry, and SEM analyses. The main focus was on the surface roughness and chemical phase composition of the damaged zone along with the identification of fretting fatigue crack initiations over the surface of the material...