The powder of an Al7075 alloy was prepared by gas atomization. A combination of cellular, columnar, and equiaxed dendritic-like morphology was observed in individual powder particles with continuous layers of intermetallic phases along boundaries. The cells are separated predominantly by high-angle boundaries, the areas with dendritic-like morphology usually have a similar crystallographic orie...

Al7075?Cu composite joints were prepared by the squeeze overcast process. The effects of melt temperature, die and pressure on hardness ultimate tensile strength (UTS) studied. experimental results depict that is most significant process parameter affecting UTS. optimal values UTS (48 MPa) (76 HRB) are achieved at a temperature 800 °C, 250 90 MPa. Scanning electron microscopy (SEM) shows fractu...

Bu çalışmada, frezeleme işleminde ilerleme hızı parametresinin etkileri araştırılmıştır. amaçla Al7075 malzemesi diğer işleme parametreleri sabit tutularak 0.1, 0.15, 0.2, 0.25 ve 0.3 mm/dev hızları ile frezelenmiştir. Her bir değeri için parça boyunca kanal yapılmıştır. Frezeleme sırasında iş parçasında bağlı cihaz titreşim ölçülmüştür. Titreşim değerleri istatistiksel olarak değerlendirilmiş ...