Rapid solidification by planar flow casting has been found to have introduced deficiencies, viz. partial crystallinity, air pockets and compositional difference in the ribbons of rapidly solidified Ti42⋅9Cu57⋅1 alloy. In order to investigate the effects of these deficiencies on the corrosion of rapidly solidified Ti42⋅9Cu57⋅1 alloy ribbons, electrochemical behaviour of alloy ribbons has been in...

The galvanic corrosion behavior of Alloy 690 coupled with magnetite has been investigated in an alkaline solution at 30 °C and 60 °C using a potentiodynamic polarization method and a zero resistance ammeter. The positive current values were recorded in the galvanic couple and the corrosion potential of Alloy 690 was relatively lower. These results indicate that Alloy 690 behaves as the anode of...

Efforts to develop metallic zinc for biodegradable implants have significantly advanced following an earlier focus on magnesium (Mg) and iron (Fe). Mg and Fe base alloys experience an accelerated corrosion rate and harmful corrosion products, respectively. The corrosion rate of pure Zn, however, may need to be modified from its reported ~20 μm/year penetration rate, depending upon the intended ...

The overly-fast degradation rates of magnesium-based alloys in the biological environment have limited their applications as biodegradable bone implants. In this study, rare earth element yttrium (Y) was introduced into AZ61 magnesium alloy (Mg-6Al-1Zn wt %) to control the degradation rate by laser rapid melting. The results showed that the degradation rate of AZ61 magnesium alloy was slowed do...

The chemical degradation of alloy components in sulfur-containing environments is a major concern in oil and gas production. This paper discusses the effect of elemental sulfur and its simplest anion, sulfide, on the corrosion of Cr-Mo alloy steel at pH 2 and 5 during 10, 20 and 30 h immersion in two different solutions. 4130 Cr-Mo alloy steel is widely used as tubing and tubular components in ...

The stability of an electrodeposited nanocrystalline Ni-based alloy coating in a H₂S/CO₂ environment was investigated by electrochemical measurements, weight loss method, and surface characterization. The results showed that both the cathodic and anodic processes of the Ni-based alloy coating were simultaneously suppressed, displaying a dramatic decrease of the corrosion current density. The co...

In this study we examined the hypothesis based on relevant literature survey that the in vitro corrosion behavior of a Cobalt-chrome dental casting alloy for metal-ceramic restorations is better than that of a Nickel-chrome dental casting alloy. The corrosion released metal ions were analysed by Inductively Coupled Plasma-Atomic Emission Spectroscopy. Moreover, the specimens were electrochemica...

Study of the corrosion behaviour of a magnetron sputtered Al–Cu/Al–Cu–Mg model alloy couple in sulphate solutions has been undertaken to gain insight into the galvanic coupling between the matrix and SAl2CuMg particles in the 2024 aluminium alloy (AA2024). Polarisation curves and local electrochemical impedance spectroscopy measurements (LEIS) were performed on the individual alloys and on the ...

Magnesium (Mg) is becoming increasingly popular for orthopaedic implant materials. Its mechanical properties are closer to bone than other implant materials, allowing for more natural healing under stresses experienced during recovery. Being biodegradable, it also eliminates the requirement of further surgery to remove the hardware. However, Mg rapidly corrodes in clinically relevant aqueous en...

Eight retrieved metal-on-metal total hip replacements displayed corrosion damage along the cobalt-chromium alloy liner taper junction with the Ti alloy acetabular shell. Scanning electron microscopy indicated the primary mechanism of corrosion to be grain boundary and associated crevice corrosion, which was likely accelerated through mechanical micromotion and galvanic corrosion resulting from ...