in this study, magnetic iron oxide nanoparticles (fe3o4) with the size range of 20-30 nm were prepared by the modified controlled chemical co-precipitation method from the solution of ferrous/ferric mixed salt-solution in alkaline medium. in this process polyethylene glycol was used as a surfactant to prevent the solution from agglomeration. the prepared magnetic nanoparticles were characterize...

We present an efficient approach to develop cellulose nanocrystal (CNC) hybrids with magnetically responsive Fe3O4 nanoparticles that were synthesized using the (Fe3+/Fe2+) coprecipitation. After 2,2,6,6-tetramethylpiperidine-1-oxyl radical (TEMPO)-catalyzed oxidation of CNC, carbodiimide (EDC/NHS) was used for coupling amine-containing iron oxide nanoparticles that were achieved by dopamine li...

in this report, magnetic iron oxide nanoparticles were synthesized via coprecipitation of fe2+ and fe3+ with ammonium hydroxide, and the surface of synthesized nanoparticles was organically functionalized by commercially available amine coupling agent namely, 3-aminopropyl trimethoxysilane (apts) by using well-known sol–gel method. further reaction of the synthesized fe3o4@apts core-shell magne...

The photocatalysis of phenol was studied using Fe3O4/ZnO core/shell magnetic nanoparticles (MNPs). The photocatalysts were synthesized by coating of ZnO onto the magnetite by precipitation method and characterized by XRD, SEM and FTIR measurements. Using the Taguchi method, this study analyzes the effect of parameters such as calcinations time, calcinations temperature and molar ratio of Fe3O4:...

Superparamagnetic Fe3O4 nanoparticles are appealing materials for heat activated killing of cancer cells. Here, we report a novel method to enhance the heat activated killing of cancer cells under an AC magnetic field (AMF) by introducing a polyaniline impregnated shell onto the surface of Fe3O4 nanoparticles. These polyaniline shell cross-linked magnetic nanoparticles (PSMN) were prepared by i...

Magnetic core/shell nanospheres (MCS) were synthesized by a novel and facile one-step hydrothermal method. Supported manganese oxide nanoparticles (Fe3O4/C/Mn) were obtained from various methods (including redox, hydrothermal and impregnation) using MCS as the support material and potassium permanganate as the precursor of manganese oxide. The Mn/MCS catalysts were characterized by a variety of...

Radar absorbing materials, i.e. magnetite (Fe3O4) coated carbon fibers (MCCFs) were fabricated by electro-deposition technique. Black-colored single spinel phase Fe3O4 nanoparticles was easily synthesized by hydrothermal method using reduction of a Fe (III) - Triethanolamine complex in an aqueous alkaline solution at 60-80 ◦C. Uniform and compact Fe3O4 films were fabricated on nitric acid treat...

In this study, xanthine oxidase immobilized silica coated Fe3O4 nanoparticles (Fe3O4@SiO2-XO) were successfully prepared and characterized by transmission electron microscope, X-ray powder diffraction, Fourier transform infrared spectroscopy and vibrating sample magnetometer. The average diameter of the Fe3O4 nanoparticles was about 300 nm to 350 nm with a shell thickness of 60 nm. The maximum ...

The aim of this study was to fabricate biodegradable poly-L-lactic acid (PLLA) bone screws containing iron oxide (Fe3O4) nanoparticles, which are radiopaque and 3D-printable. The PLLA composites were fabricated by loading 20%, 30%, and 40% Fe3O4 nanoparticles into the PLLA. The physical properties, including elastic modulus, thermal properties, and biocompatibility of the composites were tested...

an innovative method based on the membrane bioreactor (mbr) technology was developed as a potential remedy for the water shortage. mbrs attracted much attention in the field of wastewater treatment and reuse. it is reported from many researchers that membrane bioreactor technology is feasible and an efficient method for the treatment of wastewater. however, mbrs are faced to membrane fouling whic...