The purpose of this study was to evaluate hardness (indicator for polymerization) and thickness of two types of resin cement at coronal, middle and apical level of tooth root canal. Ten extracted maxillary incisors were instrumented and post space was prepared for cementation of titanium post. Samples were divided into two groups and each group was cemented either of the two types of resin ceme...

BACKGROUND There are a number of studies citing the primary reason for replacing auto cure glass ionomer cements was due to recurrent caries. The purpose of this study was to use an in vitro model to measure caries at the dentine restoration interface of bonded composite resin and auto cure glass ionomer cement restorations and to measure the amount of surface degradation occurring in the resto...

Aim: To evaluate the long-term post push-out bond strength to dentin, water sorption, solubility and swelling of conventional and self-adhesive dual-cure resin cements. Methods: Forty-eight bovine roots were prepared for fiber post cementation with RelyX ARC and RelyX U100. According to resin cement and storage time (24 h and 6 months), 4 groups were assessed using the push-out test. Water sorp...

OBJECTIVES To evaluate the effect of photo-irradiation time to the adhesive on the regional bond strength of a dual-cure resin core material to root canal dentine using photo and dual-cure adhesives with self-etching primer. MATERIALS AND METHODS Post spaces were prepared in extracted premolars and then the root canal dentine was treated with one of the following bonding procedures: (1) Clear...

The aim of this study was to evaluate the effect of silanization protocols on the bond strength of two resin cements to a lithium disilicate glass-ceramic. Thirty-two ceramic discs were assigned to 2 groups (n=16): G1 - dual-cured resin cement and G2 - light-cured resin cement. Four subgroups were evaluated according to the used silanization protocol. The glass-ceramic was etched with 10% hydro...

OBJECTIVE To evaluate the effects of etch-and-rinse and self-etching adhesive systems on Vickers hardness (VHN) uniformity of dual-cured resin cements after fiber post cementation. METHODS FIFTY GLASS FIBER POSTS WERE CEMENTED INTO BOVINE ROOTS USING THE FOLLOWING CEMENTING SYSTEMS: Prime&Bond 2.1 Dual Cure and Enforce with light-activation (PBDC-LCEN); Prime&Bond 2.1 and Enforce with light-a...

OBJECTIVES To determine the micro-hardness profile of two dual cure resin cements (RelyX-U100, 3M-eSPe and Panavia F 2.0, Kuraray) used for cementing fiberre inforced resin posts (Fibrekor-Jeneric Pentron) under three different curing protocols and two water storage times. MATERIAL AND METHODS Sixty 16 mm long bovine incisor roots were endodontically treated and prepared for cementation of th...

Objective: The purpose of this study was to investigate the effects different surface treatments on fracture strength zirconia-based ceramic restorations. Methods: Each 120 dental implant abutments and analogs were used in present study. Zirconia core materials manufactured implants by using CAD/CAM device they randomly divided into 6 groups (n=20) according pretreatments; control group (Group ...

OBJECTIVE The objective of this study was to evaluate the effect of desensitizing agents containing different amounts of fluoride on the shear bond strength of a dual polymerized resin cement and a resin-modified glass ionomer cement (RMGIC) to dentin. MATERIAL AND METHODS One hundred human molars were mounted in acrylic resin blocks and prepared until the dentin surface was exposed. The spec...