Nickel oxide nanostructures with different lengths have been easily synthesized by calcining nickel foil after soaking in LiOH solution of different concentrations. The measurements of electrochemical properties of these NiO nanostructures show that different lengths of NiO nanostructures would have different electrochemical properties and the NiO nanowires with the longest length have the larg...

Potentially toxic elements (PTEs) including nickel and chromium are often present in soils overlying basalt at concentrations above regulatory guidance values due to the presence of these elements in underlying geology. Oral bioaccessibility testing allows the risk posed by PTEs to human health to be assessed; however, bioaccessibility is controlled by factors including mineralogy, particle siz...

Nickel oxide thin film of various preferred orientations was deposited using sol-gel method using solvents including methanol. The resulting film was analyzed using X-ray diffraction (XRD), scanning electron microscopy (SEM), contact angle measurement, and ultraviolet spectroscopy (UV-vis). Antibacterial activities of nickel oxide-based film against gram-negative bacteria (Escherichia coli) has...

Bi-stable switching effect has been studied in nickel oxide films with three different thicknesses. The best sample of our experiments was 150-nm NiO film. Its resistance ratio between high and low states was 3.6 in endurance measurement. The maximum resistance ratio in I–V curve could reach two orders of magnitude, and it could endure over 200 times of reverse processes with the ratio remainin...

The gas temperature of atomospheric gas in a graphite atomizer was measured during an atomization stage in graphite furnace atomic absorption spectrometry (GF-AAS), by using a two-line method under the assumption of Boltzmann distribution. Iron and nickel were chosen as the probe elements to compare the gas temperatures obtained with different pairs of spectral lines. The atomic absorptions of ...

The partial oxidation of methane to syngas was studied in this work over Ni-containing ceria catalysts with nickel content of 5, 10 and 20 at.% at atmospheric pressure. All catalysts, in the as prepared state, showed similar activity and CO selectivity at T ≥ 550◦C. Catalyst pre-reduction was not required. Reaction mixtures were dilute, containing 3 mol% CH4 and 1.5 mol% O2. Methane conversion ...

A sonochemistry-based synthesis method was used to produce nanocrystalline nickel oxide powder with ≈ 20 nm average crystallite diameter from Ni(OH)(2) precursor. Ultrasound waves were applied to the primary solution to intensify the Ni(OH)(2) precipitation. Dried precipitates were calcined at 320°C to form nanocrystalline NiO particles. The morphology of the produced powder was characterized b...

La0.8Sr0.2CoO3 was coated on NiO (LSC–NiO) cathodes using a sol–gel method. Dissolution studies in molten Li2CO3 and K2CO3 (62:38 mol%) at 650 8C showed lower Ni dissolution than that of the conventional nickel oxide cathode. Impedance analysis showed that the behavior of the developed cathode is similar to that of nickel oxide. The LSC coated Ni cathode has an over potential of 109 mVat an app...

The use of dead biomass of the fungus Hypocrea lixii as a biological system is a new, effective and environmentally friendly bioprocess for the production and uptake of nickel oxide nanoparticles (NPs), which has become a promising field in nanobiotechnology. Dead biomass of the fungus was successfully used to convert nickel ions into nickel oxide NPs in aqueous solution. These NPs accumulated ...

Nickel and aluminum powders were mechanically alloyed with 10 or 30 vol.% refractory metal powders (molybdenum or tungsten) for times up to 50 h. Intermetallic synthesis takes place after lo-20 h alloying, with concomitant dispersion of the inert refractory metal phase, resulting in an NiAl matrix containing fine refractory dispersoids. The reactive synthesis step is direct, without intermediat...