This paper reports the formation of self-organized nanoporous gallium oxide by anodization of solid gallium metal. Because of its low melting point (ca. 30 °C), metallic gallium can be shaped into flexible structures, permitting the fabrication of nanoporous anodic oxide monoliths within confined spaces like the inside of a microchannel. Here, solid gallium films prepared on planar substrates w...

The photoelectrochemical response of nanoporous films, obtained by anodization of Ti and W substrates in a variety of corrosive media and at preselected voltages in the range from 10 to 60 V, was studied. The as-deposited films were subjected to thermal anneal and characterized by scanning electron microscopy and X-ray diffraction. Along with the anodization media developed by previous authors,...

PURPOSE The aim of the presented research was to find a combination of surface modification methods of implants made of the Ti-6Al-4V ELI alloy, that lead to formation of effective barrier for metallic ions that may infiltrate into solution. METHODS To this end, the following tests were carried out: roughness measurement, the voltamperometric tests (potentiodynamic and potentiostatic), and th...

Focused ion beam lithography and a two-step anodization have been combined to fabricate a vertical fan-out platform containing an array of unique probes. Each probe comprises three anodic alumina nanochannels with a fan-out arrangement. The lithography is used to pattern an aluminum sheet with a custom-designed array of triangular 'cells' whose apexes are composed of nanoholes. The nanoholes gr...

Due to the broad applications of porous alumina nanostructures, research on fabrication of anodized aluminum oxide (AAO) with nanoporous structure has triggered enormous attention. While fabrication of highly ordered nanoporous AAO with tunable geometric features has been widely reported, it is known that its growth rate can be easily affected by the fluctuation of process conditions such as ac...

To improve the photo-catalytic degradation of salicylic acid, we reported the fabrication of ordered TiO2 nanotube arrays by a simple and effective two-step anodization method and then these TiO2 nanotubes were treated in a methanol solution under UV light irradiation. The TiO2 nanotubes prepared in the two-step anodization process showed better photo-catalytic activity than those prepared in o...

Novel biomedical titanium (Ti) implants with high osteogenic ability for fast and good osseointegration under normal as well as osteoporotic conditions are urgently needed. Expanding on our previous in vitro results, we hypothesized that nanotubular, strontium-loaded (NT-Sr) structures on Ti implants would have favorable osteogenic effects and evaluated the in vivo osseointegration of these imp...

The Ti foil (0.1 mm thickness, 99.6 % purity, Goodfellow, England) was cleaned by using distilled water and acetone and dried off with N 2 gas. The bare Ti foil was anodized in an ethylene glycol solution containing NH 4 F (0.38 wt%) and H 2 O (1.79 wt%) and placed in a well-insulated bath for 3 h at 30 V and at 20 ℃ using a dc power supply (N5753A model, Agilent). The textured Ti surface was o...

With the aim of developing a process for surface enlargement on an electrode for measuring brain activity attempts have been made to fabricate a porous anodic alumina membrane directly on the electrode. The porous membrane was intended to be used as scaffold for deposition of an electrically conducting polymer on the electrode surface. A silicon wafer with gold electrodes was the base onto whic...

Highly ordered TiO2 nanotube arrays on Ti substrates were prepared by an electrochemical anodization process in a mixture of glycerol and water containing 0.5 wt% NH4F and then thermally annealed from 400 C to 600 C. The sample structures were characterized by scanning electron microscopy and X-ray diffraction measurements, where the nanotube pore diameter and length were found to increase with...