Corrosion prevention in biomaterials has become crucial particularly to overcome inflammation and allergic reactions caused by the biomaterials' implants towards the human body. When these metal implants contacted with fluidic environments such as bloodstream and tissue of the body, most of them became mutually highly antagonistic and subsequently promotes corrosion. Biocompatible implants are ...

The electrochemical behavior of polycrystalline TiO₂ anatase coatings prepared by a one-step hydrothermal synthesis on commercially pure (CP) Ti grade 2 and a Ti13Nb13Zr alloy for bone implants was investigated in Hank's solution at 37.5 °C. The aim was to verify to what extent the in-situ-grown anatase improved the behavior of the substrate in comparison to the bare substrates. Tafel-plot extr...

The corrosion behavior of mild steel in the presence of acetic acid (CH3COOH) and carbon dioxide (CO2) has been investigated using electrochemical techniques and weight-loss measurements. Electrochemical measurements have shown that the presence of acetic acid affects predominantly the cathodic reaction. The acetic acid effect is much more pronounced at elevated temperatures when catastrophic c...

This paper addresses investigation of the corrosion behavior of copper bearing anodes with high nickel content. Anodes are produced from different solid wastes formed during the copper or nickel row materials treatment. Nickel content in anode samples had values up to 10 mas %. The content of tin, lead and antimony was up to 1 % for each of elements. Sulphuric acid solution, concentration of 17...

This work reports the effects of water flow and dissolved oxygen (DO) on corrosion behavior of reduced activation ferritic/martensitic steel, F82H. The corrosion tests were performed in high temperature pressurized water by using a test apparatus for rotated disk sample. All of specimens showed weight gains after static corrosion tests up to 500 h. However, the rotated disk showed weight losses...

The novel Cr-containing low alloy steels have exhibited good corrosion resistance in CO₂ environment, mainly owing to the formation of Cr-enriched corrosion film. In order to evaluate whether it is applicable to the CO₂ and H₂S coexistence conditions, the corrosion behavior of low-chromium steels in CO₂-H₂S environment with high pressure and high temperature was investigated using weight loss m...

The corrosion behavior of oxygen-free copper in anoxic sulfide solutions under nuclear waste disposal conditions was studied using electrochemical impedance spectroscopy (EIS), scanning electron microscopy (SEM) equipped with a focused ion beam (FIB), X-ray photoelectron spectroscopy (XPS) and Micro X-ray diffraction ( XRD). The film growth process and mechanism were elucidated using an Au mark...

The corrosion behavior of X80 steel in the presence of coupled coating defects was simulated and studied under the interference of alternating current (AC) in an alkaline environment. The results from electrochemical measurements showed that the electrode potential of the coating defect with the smaller exposed area was lower than that with the larger area, which indicated that the steel with t...

The corrosion behavior of pure Fe under a Na₂SO₄ deposit in an atmosphere of O₂ + H₂O was investigated at 500 °C by thermo gravimetric, and electrochemical measurements, viz. potentiodynamic polarization, electrochemical impedance spectroscopy (EIS), and surface characterization methods viz. X-ray diffraction (XRD), and scanning electron microscope (SEM)/energy dispersive spectroscopy(EDS). The...

Aluminum based metal matrix composites (MMCs) have received considerable attention in the automotive, aerospace and nuclear industries. One of the main challenges using Al-based MMCs is the influence of the reinforcement particles on the corrosion resistance. In the present study, the corrosion behavior of Al-B₄C MMCs in a 3.5 wt.% NaCl solution were investigated using potentiodynamic polarizat...