in this work, electrochemical methods such as tafel polarization and electrochemical impedance spectroscopy (eis) were used to study the inhibition efficiency of nettle leaves hydroalcoholic extract as a green corrosion inhibitor of api 5l carbon steel in 0.5 m h2so4 solution. the results showed that the inhibition efficiency was increased with increasing the concentration of the extract and th...

The corrosion inhibition of AISI309 austenitic stainless steel by 2,2'-Bipyridyl in 0.5M H 2 SO 4 at 298K was studied using the mass loss’ method, the potentiodynamic polarization (Tafel), the linear polarization (LRP) and the electrochemical impedance spectroscopy (EIS). The results showed a mixed inhibition mode and an increase in the charge transfer resistance, due to inhibitor molecules’ ad...

In this work, the extract of the leaves and berries of solanum nigrum was examined as a green corrosion inhibitor for zinc in 0.5N HCl by using weight loss, gasometric and thermometric methods. Results obtained showed that the extract of solanum nigrum offered good protection against corrosion of zinc metal and exhibited high inhibition efficiencies. The inhibition efficiency was found to incre...

The potential cytotoxicity on vascular smooth muscle cells of corrosion products from 316 L stainless steel, one of most popular biomaterials of intravascular stents, has not been highlighted. In this investigation, 316 L stainless steel wires were corroded in Dulbecco's modified eagle's medium with applied constant electrochemical breakdown voltage, and the supernatant and precipitates of corr...

2-(1-methyl-4-((E)-(2-methylbenzylidene)amino)-2-phenyl-1H-pyrazol-3(2H)-ylidene)-hydrazineecarbothioamide (HCB) was synthesized as a corrosion inhibitor from the reaction of 4-aminoantipyrine, thiosemicarbazide and 2-methylbenzaldehyde. The corrosion inhibitory effects of HCB on mild steel in 1.0 M HCl were investigated using potentiodynamic polarization (PDP) and electrochemical impedance spe...

Several works have been done and more are on the pipeline on the influence of organic compounds containing polar functions on the corrosion inhibition of metals in various aqueous media. Corrosion inhibition by such compounds is generally attributed to their adsorption on the metal/solution interface. The specific action of an inhibitor depends on the nature of its interaction with metal surfac...

The corrosion inhibitive action of flower extracts of Clitoria ternata flower on mild steel corrosion in 0.5 M H2SO4 solution was studied using weight loss method, potentiodynamic polarization and EIS measurements. The results obtained indicate that the extracts functioned as good inhibitors in 0.5 M H2SO4 solution. Inhibition efficiency was found to increase with extract concentration. The ads...

Organosilanes are candidates to replace chromates as metal surface pretreatments to inhibit corrosion. Current research shows that silane films are strictly water barriers and show no electrochemical corrosion inhibition. To improve the corrosion performance of silane film, therefore, the foremost objective is to improve water resistance. An understanding the interaction of silane with water is...

The influence of the concentration of1-H-benzoteriazolon the corrosion of 316 stainless steel (SS) in chloride acid 1M solutions was studied. The potentiodynamics polarization and scanning electron microscopy (SEM) have been used. The inhibition efficiency increased with an increase in the concentration of1-H-benzoteriazol.The adsorption of1-H-benzoteriazol onto the SS surface occurs accord...

The corrosion inhibitive action of oxystelma esculentum stem on mild steel corrosion in 0.5 M H2SO4 solution was studied using weight loss method, potentiodynamic polarization and EIS measurements. The results obtained indicate that the extracts functioned as good inhibitors in 0.5 M H2SO4 solution. Inhibition efficiency was found to increase with extract concentration. The adsorption of consti...