A research on the corrosion inhibition of mild steel pitting corrosion in concrete pore solution by sodium nitrite was carried out by employing potentiodynamic, potentiostatic polarization and zero resistance ammetery (ZRA) techniques. Passivity breakdown potential was decreased from the transpassive potential of 700 mV at the absence of chloride to a value of -50 mV when just 0.01M NaCl was ad...

S. Lasek, E. Mazancová, VŠB-Technical University of Ostrava, FMMI Czech Republic In this paper corrosion properties of X70MnAl28-9 TRIPLEX steel were tested after hot rolling and subsequent aging at 500 °C for 6, 30 and 60 min. and at 600 °C for the same times. For comparison related steels(X100MnAl28-12, X70Mn22, C20) were also used. The microstructure wascharacterized by light microscopy, SEM...

Statistical models have been developed to predict the occurrence of pitting corrosion in carbon steel waste storage tanks exposed to radioactive nuclear waste. The levels of nitrite concentrations necessary to inhibit pitting at various temperatures and nitrate concentrations were experimentally determined via electrochemical polarization and coupon immersion corrosion tests. Models for the pit...

AISI 304L austenitic stainless steel with different grain sizes of 0.5 -12 μm was obtained through the martensitic process. Corrosion behavior of different samples was investigated in a 0.5M HCl solution using open circuit potential, potentiodynamic polarization and electrochemical impedance spectroscopy tests. Also, the correlation between the grain size and pitting corrosion resistance was as...

OBJECTIVE To analyze the effect of various coating formulations on the mechanical and corrosion properties of nickel-titanium (NiTi) orthodontic wires. MATERIALS AND METHODS Uncoated, rhodium-coated, and nitrified NiTi wires were observed with a three-point-bend test, surface roughness (Ra) measurement, scanning electron microscopy, energy dispersive spectroscopy, and electrochemical testing ...

To achieve good corrosion resistance in a weld is much more challenging than for plate or sheet material, which has undergone controlled rolling, heat treatment and pickling processes in the steel mill. The choice of weld procedure and parameters, filler metal and shielding gas all play important roles. For duplex and lean duplex grades it is essential to ensure that an adequate amount of auste...

The simultaneous fluctuations of potential noise and current noise between two nominally identical X-65 mild steel electrodes were recorded using a ZRA (Zero Resistance Ammeter) to monitor localized CO2 corrosion in CO2-saturated 1 wt % NaCl solution at 80C. Electrochemical noise (EN) was obtained from both 11.6 cm and 1 cm specimens to understand how the surface area affects EN signals. Linear...

The AISI 316 L Stainless Steel (SS) specimens were exposed to passivation surface through two different processes including; holding in 40-vol% HNO3 at temperature of 60 ºC for 30 min and 15-vol%H2SO4 at ambient temperature for 1 hour. The corrosion behavior of specimens was evaluated in physiological solutions by electrochemical in vitro tests through linear an...

In this study, an attempt was made to minimize the corrosion rate and maximize pitting potential of dissimilar metal welded joints of A387-Gr91/AISI316 steels. Process parameters of the pulsed current gas tungsten arc welding (PCGTAW) including of peak current (P), background current (B), pulse frequency (F), and on time percentage (O) were chosen as the influencing factors on corrosion behavio...

Potentiodynamic polarization and impedance tests were carried out on 316L stainless steel with culturing murine fibroblast L929 cells to elucidate the corrosion behaviour of 316L steel with L929 cells and to understand the electrochemical interface between 316L steel and cells, respectively. Potential step test was carried out on 316L steel with type I collagen coating and culturing L929 cells ...