High strength, wrought 7xxx (Al-Zn-Mg) and Al-Li based alloys show a propensity for fatigue macroscopic crack deflections aligned along grain boundaries. The present work reports a study on a 3 rd generation Al-Li based alloy in the form of a thick AA2297 (Al-Cu-Li alloy) plate, where it was found that although the lithium containing material may indeed be more susceptible to mixed mode grain b...

Many composites fail by fracture events, such as fiber breaks or matrix cracks, rather than by continuous crack growth. Conventional fracture mechanics deals with predicting crack growth. This paper suggests that conventional fracture mechanics can be extended to predict fracture events by using finite fracture mechanics. In finite fracture mechanics, the next fracture event is assumed to occur...

In this paper, the present investigation has been conducted keeping in mind some of the problems concerning the crack propagation direction and growth under constant loading in an inclined crack geometry. The present studies mainly focused on the development and modifications in the crack growth criterion to account the biaxial, shear loading and number of stress terms. Existing criteria for th...

RESTRICTIONS on the quasi-static extension, or healing, of Griffith cracks are developed in the framework of irreversible thermodynamics. It is emphasized that thermodynamics requires that (G 2r)I > 0, where i is crack speed, G the Irwin energy release rate, and 2y the work of reversible separation of the surfaces to be fractured. Implications for ‘lattice trapping’ models of cracks and for the...

Fatigue crack growth is examined in P/M 2124 aluminum alloys reinforced with SiC particles (SiCp) and whiskers (SiCw) over a wide spectrum of growth rates from 10 to 10 m per cycle. Effects of aging treatment, orientation of crack growth direction with respect to the rolling direction, mean stress (or stress ratio), and reinforcement volume percent on the fatigue crack growth threshold are inve...

The propagation of cracks in layered glass from low-velocity impact of sharp or spherical tip projectiles is observed using high-speed photography. Tests are also carried out to determine the threshold impact energy for chipping in glass blocks and subsurface crack instability in an edge-supported glass plates. The results identify the median and subsurface radial crack systems as the prime dam...

The fracture and crack growth of mechanical structures is a usual phenomenon which is due to the application of tensile, cyclic loading or thermal stresses on the structure. So introducing of methods to prevent the crack growth is useful. Afterward, one of the repairing methods of crack growth, consisting to make a hole in the crack tip to elimi-nate the sharp corners, was explained. This metho...

Applications of ceramic materials usually involve thermal stresses that can reduce their lifetime considerably. One of the most relevant mechanical properties for evaluating thermal shock damage resistance is the energy of fracture. In order to obtain this property, a stable crack growth regimen must be achieved throughout the test. In this paper, three-point bending tests are analyzed to deter...

In this work, the plastic deformation mechanisms responsible for mechanical properties and fracture toughness in nanotwinned (NT) magnesium is studied by molecular dynamics (MD) simulation. The influence of twin boundary (TBs) spacing and crack position on deformation behaviors are investigated. The microstructure evolution at the crack tip are not exactly the same for the left edge crack (LEC)...

* Corresponding author; Email: [email protected] ABSTRACT An important task in mixed-mode fracture analysis and prediction is the simulation of crack growth under mixed-mode conditions. To complete such a task, one must have (a) a computer code capable of handling the kinematics of general crack growth and determining the stress and deformation states during crack growth, and (b) a fracture crit...