The effects of environmental media on the corrosion fatigue fracture behavior of 25CrMo steel were investigated. The media include air, and a 3.5 wt.% and a 5.0 wt.% NaCl solutions. Experimental results indicate that the media induces the initiation of corrosion fatigue cracks at multiple sites. The multi-cracking sites cause the changes in the crack growth directions, the crack growth rate dur...

This article presents an experimental study on the fatigue behaviour of cracks emanating from cold-expanded holes utilizing thermoelastic stress analysis (TSA) and synchrotron X-ray diffraction (SXRD) techniques with the aim of resolving the long-standing ambiguity in the literature regarding potential relaxation, or modification, of beneficial compressive residual stresses as a result of fatig...

Fatigue crack initiation and early short crack propagation behaviour in two microstructural variants of a recently developed Low Solvus, High Refractory (LSHR) disc superalloy at room temperature has been investigated by three-point bending with replication procedure. The results shows that fine gained (FG) LSHR possesses higher fatigue life due to its better crack initiation resistance, limite...

effect of partial natural rubber replaced with synthetic rubbers, styrene butadiene and cis butadiene, on failure and strength properties of bias tread nr/br based compound was studied by efficient and conventional sulfur curing systems and mixtures of different carbon black grades. it was observed that failure behavior comprising tear resistance and crack growth in substituted compounds droppe...

Cracks and craze lines are often observed in the enamel of human teeth, but they rarely cause tooth fracture. The present study evaluates fatigue crack growth in human enamel, and compares that to the fatigue response of sintered hydroxyapatite (HAp) with similar crystallinity, chemistry and density. Miniature inset compact tension (CT) specimens were prepared that embodied a small piece of ena...

* Corresponding author; Email: [email protected] ABSTRACT Crack tunneling is a crack growth feature often seen in stable tearing crack growth tests on specimens made of ductile materials and containing through-thickness cracks with initially straight crack fronts. As a specimen is loaded monotonically, the mid-section of the crack front will advance first, which will be followed by crack growth ...

The fracture of restored teeth is a significant obstacle to lifelong oral health. Recent studies suggest that fatigue cracks originate at flaws introduced during cavity preparation and that fatigue crack growth is a principle cause of restored tooth fractures. In this study, the rate of fatigue crack growth in bovine dentin was estimated under mode I cyclic loading. Double cantilever beam (DCB)...

Recent studies have shown that nanotwinned copper (NT Cu) exhibits a combination of high strength and moderate ductility. However, most engineering and structural applications would also require materials to have superior fracture toughness and prolonged subcritical fatigue crack growth life. The current study investigates the effect of twin density on the crack initiation toughness and stable ...

Crack growth analysis has remained one of the challenging problems in the fracture mechanics of structures. On the other hand, the fatigue crack growth is a common phenomenon in the components of structures like airplanes, navies and fluid storages where the fracture due to crack should be considered in the design of these structures. In this paper, the finite volume method (FVM) is extended fo...

Fatigue crack growth is a complex process that involves interactions between many elements ranging across several length scales. This work provides an in-depth, experimental study of fatigue crack growth and the relationships between four of these elements: strain field, microstructure, crack path, and crack growth rate. Multiple data sets were acquired for fatigue crack growth in a nickel-base...