This study is to evaluate the behavior of integral and segmental specimens through static and cyclic tests. Integral specimens were made with the same size to be compared with segmental specimens that were made by connected precast members. To evaluate its bending performance and serviceability, 1 integral and 3 segmental specimens were tested under static load. And 1 integral and 2 segmental s...

Crack detection is one of the important tasks for industrial materials and products from the standpoint of safety. The assessment of the crack geometry would be a crucial parameter for quality control of products. The crack width and length could be rather easily identified by inspecting the actual surface picture. However, the depth of small crack would be difficult to estimate non-destructive...

Middle-gate is located in Hasankeyf, Batman dating back to 1800 BC and is one of the important historical structures in Turkey. The ancient structure has suffered major structural cracks due to aging as well as lateral pressure of a cracked rock which is predicted to be about 100 tons. The existing support system was found to be inadequate to support the load especially after a recent rock fall...

Failure modes in recent earthquakes on lightly reinforced shear walls includes rebar fracture and out of plane buckling of its boundary elements. In latest edition of ACI 318 and also latest amendment of NZS 3101-2006 to avoid rebar fracture in boundary elements, the minimum reinforcement ratio for shear walls is increased. This experimental study investigates that rather than increasing reinfo...

Expansion and cracking induced by the corrosion of reinforcement concrete is the major factor in the failure of concrete durability. Therefore, monitoring of concrete cracking is critical for evaluating the safety of concrete structures. In this paper, we introduce a novel monitoring method combining Brillouin optical time domain analysis (BOTDA) and fiber Bragg grating (FBG), based on mechanic...

In this paper, the sorption isotherm and the hygral deformation of a tensile strain-hardening fiber reinforced engineered cementitious composite (ECC) is described using a physical model. The influence of using a low alkali content Portland cement on the physical mechanisms of drying shrinkage is discussed. From a durability point of view the crack width of a material as a result of restrained ...