An important requirement for dental materials placed in direct contact with living tissues is biocompatibility. The purpose of this study was to evaluate the antiproliferative activity of three dental materials (mineral trioxide aggregate, zinc oxide-eugenol cement, and glass-ionomer cement) against a panel of established fibroblastic cell lines (L929, BHK21/C13, and RPC-C2A). The materials wer...

This study investigated the effects of the cement type and the water storage time on the push-out bond strength of a glass fiber post. Glass fiber posts (Fibrekor, Jeneric Pentron) were luted to post spaces using a self-cured resin cement (C&B Cement [CB]), a glass ionomer cement (Ketac Cem [KC]) or a resin-modified glass ionomer cement (GC FujiCEM [FC]) according to the manufacturers' instruct...

The aim of this study was to synthesis of glass ionomer-silk fiber composite and to evaluate the effect of adding natural degummed silk fiber on the mechanical properties of glass ionomer cement (GIC). For this purpose, natural degummed silk fibers with 1 mm in length and 13-16 µm in diameter were added to the ceramic component of a commercial glass ionomer cement in 1, 3 and 5 wt. %. Compressi...

Glass-ionomer cements were developed by Wilson and McLean at the Laboratory of the Government Chemist in England in 1965. They were a logical addition to the family of water-based dental cements, comprising silicate cement, zinc phosphate cement and zinc polycarboxylate cement. Since their commercial introduction, they are now available in essentially two types. ‘Conventional’ glass-ionomers co...

We prepared a new glass ionomer cement using bioactive CaO-P2O5-SiO2(-MgO) glass and investigated its setting process using FT-IR and MAS NMR analyses. The compressive strengths of the cements depended on the glass composition and a maximum strength of 33.3 +/- 4.7 MPa was obtained using cement with the glass composition of MgO:4.6, CaO:44.9, SiO2:34.2 and P2O5:16.3% in weight. FT-IR analysis s...

The purpose of this study was to compare regional bond strength at middle and cervical thirds of the root canal among glass fiber-reinforced composite (FRC) endodontic posts luted with different cements, using the push-out test. To compare the performance (retention) of two types of luting cements polycarboxylat cement and Glass ionomer cement used to cement translucent fibre post. and To compa...

Glass ionomer cements show great potential as low cost, minimally invasive dental restorative materials. However, their use is limited by relatively poor mechanical properties, especially fracture toughness. One possibility for improving their fracture toughness is through the addition of fluorhydroxyapatite nanoparticles, which resemble the crystals found in tooth enamel. Hydroxyapatite and fl...

The purpose of this study was to evaluate the ability of a glass-ionomer cement-base material to prevent bacterial penetration along the dentin interface and to compare it with two conventional cement-base materials. A total of 107 Class 5 restorations was placed in Rhesus monkey teeth by means of three test materials [zinc oxide-eugenol (ZOE), copalite varnish + zinc phosphate cement base (V +...

OBJECTIVE To estimate the microhardness of glass ionomer cement (vitrofil) and resin modified glass ionomer cement (vitremere) in the presence and absence of different surface protections. STUDY DESIGN An in-vitro experimental study. PLACE AND DURATION OF STUDY The Department of Operative Dentistry, Dr. Ishrat-ul-Ebad Khan Institute of Oral Health Sciences, Dow University of Health Sciences...