nickel doped tio2 nano particles (1% w/w) were prepared and immobilized on nax zeolite and after characterization by x-ray diffraction (xrd) and scanning electron microscopy (sem) used as photo catalyts for degradation of orange g. the xrd patterns show that the supported tio2 are crystallized in anatase form and the intensity of the zeolite peaks decreases with the increase of tio2 loading. sc...

Mesoporous aggregates of nanocrystalline zeolites with MFI and BEA frameworks have been synthesized using a one-pot and single structure directing agent. The effect of different reaction conditions, such as temperature, time, pH and water content, on the particle size, surface area and mesopore volume has been studied. Nanocrystalline and mesoporous ZSM-5, β and Y zeolites were modified with di...

A discussion of various strategies for the intrazeolite encapsulation of polymer filaments is given. Two examples are discussed in more detail: Poly(2-ethylaniline) and pyrolyzed polyacrylonitrile in zeolite hosts. Poly(2-ethylaniline) chains were synthesized within the three-dimensional channels of dehydrated zeolites X and Y via oxidation of the intrazeolite monomers with aqueous (NH4)2S20s. ...

NaY zeolite, an ordered, large pore molecular sieve pertaining to the FAU zeolite structural group, was studied as a novel matrix for efficient preparation of supported isothiazolinone-based biocide, and results were compared those corresponding mesoporous silicas. To analyze possibility reducing biocide ecotoxicity by encapsulation, commercial used latex preservation (CMIT/MIT) incorporated in...

In this paper, a novel nano crystalline sodalite was synthesized and characterized by XRF, XRD, SEM and FTIR analysis. Cu2O nanoparticles (30-60 nm) were loaded on nano zeolite bed and utilized as an adsorbent to remove dimethyl phthalate. The SEM-EDX of modified zeolite indicates that the amount of copper loading on the zeolite was 4.5 wt%. Modified nano zeolite was used as an effective adsorb...

Thermal decomposition in a thermobalance of Fe(CO), adsorbed on alkali-metal, hydrogen-Y, dealuminated Y, L and omega zeolites proceeds stepwise via slow decarbonylation at low and high temperatures, separated by a fast endothermic reaction. Average CO/Fe ratios have been determined after each step. From i.r. results the former intermediates are assigned to species bearing bridging CO, whereas ...

A novel confined-space synthesis method has been developed to synthesize zeolite nanocrystals. Colloidal silica nanoparticles serving as the silica source as well as the hard template were embedded in the mesoporous carbon via in situ polymerization of furfuryl alcohol (FA) in the presence of tri-block copolymer (Pluronic P123), and then reacted with an alkaline aqueous solution (Na2O-Al2O3-H2O...