This paper focuses on the effect of the viscoelasticity of the adhesive layer on the flexural creep response of reinforced concrete beams strengthened with composite materials. A theoretical model is developed, which considers the strengthened beam as a layered structure that consists of the reinforced concrete beam, the adhesive layer, and the FRP strip, and accounts for the creep of each comp...

Debonding failure is the main failure mode in flexurally strengthened reinforced concrete beams by externally bonded or near surface mounted fibre reinforced polymer (FRP) composites. It is believed that FRP debonding will be initiated if the shear stress on the concrete-FRP interface reaches the tensile strength of concrete. However, it was found through experimental and analytical studies tha...

This paper demonstrates the size effect on the shear strength of reinforced concrete (RC) beams with stirrups and does so in two separate and independent ways: (1) by fracture mechanics, based on finite-element analysis calibrated by a large beam test; and (2) by purely statistical analysis in which a newly assembled database of 234 tests is filtered to eliminate spurious size effects caused by...

Elevated rail transit has been developed in some big cities in China in recent years. However, specialized codes for design of the bridges in the elevated rail transit system have not yet been established. Based on the prestressed concrete (PC) box girder bridges on Guangzhou metro line 4, some technical features of design principle and technology requisition, ensemble plan and design load of b...

In this paper, a nonlinear finite element (FE) analysis of hybrid-steel concrete connections is presented. The detailed experimental results of the four full-scale hybrid-steel concrete connections with limited seismic detailing have been discussed in a different paper. However, due to the inherent complexity of beam–column joints and the unique features of the tested specimens, the experimenta...

With the recent development of 3D printing technology, concrete materials are sometimes used in 3D printing. Concrete structures based on 3D printing have been characterized to have the form of multiple layer build-up. Unlike general concrete structures, therefore, the 3D-printed concrete can be regarded as an orthotropic material. The material property of the 3D-printed concrete’s interface be...

Energy spectra of high-energy neutrons and neutron time-of-flight spectra were calculated for the setup of experiment T-454 performed with a NE213 liquid scintillator at the Final Focus Test Beam (FFTB) facility at the Stanford Linear Accelerator Center. The neutrons were created by the interaction a 28.7 GeV electron beam in the aluminum beam dump of the FFTB which is housed inside a thick ste...

This study focused on the residual strengths of reinforced concrete beams with heavy deterioration. This work is based on experimental investigation of reinforced concrete beams naturally corroded over 30 years. Visual inspection was firstly conducted and the concrete cracking, spalling of concrete cover, corrosion of rebar were recorded. Material tests on concrete and corroded rebar were also ...

The aim of this paper is to present results of testing a full scale reinforced concrete T connection by static loading. The connection represents a beam-column connection. The beam and column had a square cross section with a 300 mm dimension. The height of the column was 2.9 m and the clear beam length was 1.4 m. The connection was initially tested to failure. Galvanised steel straps were used...

This study is concerned with the use of the concrete samples produced by tincal concentrator waste as a gamma radiation shield. The values of mass attenuation coefficients for concrete samples measured at 59.54 (Am-241) and 80.99 (Ba-133) keV photon energies. Gamma rays were counted by a NaI(Tl) detector coupled to multi channel analyzer (MCA) using narrow beam transmission arrangement. Theoret...