We have successfully prepared α-Fe2O3 nanospheres by solvothermal method using 2-butanone and water mixture solvent for the first time, which were about 100 nm in diameter and composed of very small nanoparticles. The as-prepared samples were characterized using X-ray diffraction, scanning electron microscopy, and transmission electron microscopy. The results showed that the product was α-Fe2O3...

the reaction kinetics of the isomerization 3,4-dichlorobutene-1 to 1,4-dichlorobutene-2 was investigated by using gas-liquid chromatography method in the presence of fe2o3/mgo as solid catalyst in the temperature range 25-55°c. fe2o3/mgo has been prepared by the support saturation method, tested in the isomerization of 3, 4-dichlorobutene-1 into 1, 4-dichlorobutene-2. this catalyst shows a high...

Polycarbazole (PCz) has been synthesized by chemical oxidation method using APS as an oxidizing agent and PCz/CuO PCz/Fe2O3 nanocomposites in situ polymerization for different wt% of CuO Fe2O3 at room temperature. XRD patterns confirmed crystalline nature samples. FTIR indicated strong interaction between PCz nano fillers. The morphological optical absorption studies were carried out SEM UV–Vis...

A novel and simple preparation of amine-modified γ-Fe2O3 nanoparticles is described. The presence of amine groups on the surface, instead of hydroxyl groups, will allow conjugation of biologically active molecules to the iron oxide nanoparticles without the need for a size increasing silica shell. Furthermore, the outer amine-layer increases the temperature of the γ-Fe2O3 to α-Fe2O3 structural ...

the reduction of fe2o3 powder at the top layer by the volatiles from high volatile (hv) bituminous coalat the bottom layer of a multilayer powder geometry including a separating alumina layer was studied.the simultaneous effects of the alumina layer thickness, time, temperature and the weight of coal onthe amount of reduction and coal devolatilization were studied by implementing a rotatable ce...

The studies include the results and discussion related with reaction of Fe2O3 with Na2SO4 in presence of SO2 (g) at 800 and 900 C. The iron oxides are produced by the oxidation of iron base alloys in many industrial operations. The metal oxide undergoes certain high temperature chemical reactions in presence of a gas (such as SO2) and molten salts (say Na2SO4). The thermo-gravimetric studies h...

In order to create Fe2O3 and Fe2O3·H2O nanoparticles, various polymers were used as dispersing agents, and the resulting effects on the dispersibility and nanoparticulation of the iron oxides were evaluated. It was revealed that not only the solution viscosity but also the molecular length of the polymers and the surface tension of the particles affected the dispersibility of Fe2O3 and Fe2O3·H2...