The main objective of this study was to determine the mold resistance and mechanical properties of fungicide-treated wood and bamboo flour/high density polyethylene (HDPE) composites. Zinc borate (ZB), 4,5-dichloro2-octyl-isothiazolone (DCOIT), zinc pyrithione (ZPT), and carbendazim (MBC) were used as fungicides. Then, treated and untreated samples were exposed to mold fungi (Aspergillus niger,...

To investigate the possibility of using bamboo-bundle laminated veneer lumber (BLVL) as a cooling tower packing material, the water absorption rates, thickness swelling rates, and flexural properties of three different composite materials were studied. The BLVL was combined with either 12% or 24% phenol formaldehyde resin (PF), and the moso bamboo strips were exposed to water baths at three dif...

A method is presented for reconstructing the geometry, pith, knots and local fibre orientations in timber boards, based on X-ray computed tomography scans. The deviations around were found by a new algorithm, image analysis. experimental data comprised scans, eigenfrequency measurements four-point bending tests of 20 Norway spruce boards. 3D 1D finite element models pure zone created, accountin...

This paper investigated the potentiality of muli (Melocanna baccifera) for making bamboo mat plywood. Bamboo mat plywood with the length, width and thickness of 2.4 m × 1.2 m × 7 mm was made using liquid urea formaldehyde resin. The physical and mechanical properties of such plywood were compared with the existing market plywood. The average density of bamboo mat plywood was much higher compare...

Successful development of an appropriate tree breeding strategy and wood utilization requires information on wood properties. This study was therefore conducted to assess wood density and mechanical properties of Pinus kesiya Royle ex Gordon grown in Malawi. Wood samples from six families of P. kesiya at the age of 30 years were used for the study. The estimated mean wood density, Modulus of El...

The reusability of decommissioned treated wood is primarily dependent on the residual strength of the wood after service. Determining the residual strength can provide useful information for structural design and reuse of the decommissioned treated wood. This study evaluated the residual strength of decommissioned chromated copper arsenate–treated utility pole wood. Eleven decommissioned southe...

The reusability of decommissioned treated wood is primarily dependent on the residual strength of the wood after service. Determining the residual strength can provide useful information for structural design and reuse of the decommissioned treated wood. This study evaluated the residual strength of decommissioned chromated copper arsenate-treated utility pole wood. Eleven decommissioned southe...

the aim of this study was to explore the minimum amount of urea formaldehyde (uf) resin content and optimum particleboard density while maintaining boards’ quality to reduce production costs. board density at three levels (520, 620 and 720 kg m-3) and resin content (6, 7 and 8%) were variable parameters. stepwise multivariate linear regression models were used to evaluate the influence of board...

The modulus of elasticity and bending strength 45 structural Salzmann pine timber pieces with nominal dimensions 150x200x5400 mm3 from an existing 18th century structure were estimated by semi-destructive density estimation probing method (drilling chips extraction) acoustic wave velocity (stress ultrasound wave). Bending strength, obtained according to the EN 408 European standard, visual grad...

The permanent deformation pavement of roads and streets at tropical zones Abstract (if layers are sufficiently compacted) is due to increase of asphalt layers temperature and consequential decrease of modulus of elasticity. Therefore, the asphalt mixture moves aside of the wheels of heavy vehicles and cause permanent deformations without volume variation. On the other hand, if the asphalt layer...