Solar cells consisting of an extremely thin In2S3/CuInS2 buffer/absorber layer uniformly covering planar ZnO were prepared entirely by chemical spray pyrolysis. Au nanoparticles (Au-NPs) were formed via thermal decomposition of a gold(III) chloride trihydrate (HAuCl4·3H2O) precursor by spraying 2 mmol/L of the aqueous precursor solution onto a substrate held at 260 °C. Current-voltage scans and...
We have used an inexpensive high-frequency ultrasound generator from a household humidifier to create a useful source for ultrasonic spray pyrolysis and produced submicrometer silica particles that are porous on the nanometer scale. By using two heated zones, we first initiate polymerization of organic monomers in the presence of silica colloid, which creates in situ a composite of silica with ...
Monocrystalline cubic and/or monoclinic Y2O3:Eu nanoparticles (10-50 nm) were synthesized continuously without post-processing by single-step flame spray pyrolysis (FSP). These particles were characterized by Xray diffraction (XRD), nitrogen adsorption (BET) and transmission electron microscopy (TEM). Photoluminescence (PL) emission was measured as well as the time-resolved PL-intensity decay. ...
Silver particles less than 20 nm in diameter were synthesized by pyrolysis of an ultrasonically atomized spray of highly dilute aqueous silver nitrate solution at temperatures above 650◦C and below the melting point of silver. Feed solution concentration and ultrasound power applied to the atomizer were found to have a significant impact on the particle size of the silver nanoparticles. Average...
Spray pyrolysis has been used to prepare La0.6 Sr0.4Co0.2Fe0.8O3-δ thin film cathodes for solid oxide fuel cell (SOFC) applications. The films are polycrystalline with nano-meter sized grains and less than 1 μm in thickness. Deposition parameters for film deposition have been established. The ratio of deposition temperature to solvent boiling point is found to be the most important processing p...
Transparent conducting tin oxide thin films have been prepared by electron beam evaporation and spray pyrolysis methods. Structural, optical and electrical properties were studied under different preparation conditions like substrate temperature, solution flow rate and rate of deposition. Resistivity of undoped evaporated films varied from 2⋅65 × 10 Ω-cm to 3⋅57 × 10 Ω-cm in the temperature ran...